Abstract:In this paper, excellent performance W-Cu-Ni-Fe alloys with the addition of Ni and Fe (total content: 5 wt%) were successfully prepared by low temperature liquid-phase sintering, using the raw material of ultrafine W-Cu-Ni-Fe composite powder. Ultrafine W-Cu-Ni-Fe composite powder with high sintering activity and uniform composition distribution was prepared by a two-stage reduction method consisting of carbothermal reaction and hydrogen deep deoxidation. Additions of Ni and Fe not only improved the wettability between W and Cu two phases, but also improved the bonding strength of two-phase interface. All sintered samples had higher relatively densities to ensure that the samples have great comprehensive properties. When Ni and Fe were co-added in appropriate proportions, the highest tensile strength and elongation of W-Cu-Ni-Fe alloy samples were 497 MPa and 9.12 % for the composition: W-3.5 wt%Ni-1.5 wt%Fe-25 wt%Cu, respectively. Meanwhile, with increasing Ni content from 0 wt% to 5 wt%, the compressive strength and failure strain of alloy samples increased from 1160 MPa to 2376 MPa and from 53 % to 98 %, respectively. In addition, with the enhancement of the solid solution strengthening effects of Ni and Fe on Cu matrix, the bending strength and microhardness of the alloy samples increased to 1174 MPa and 361 HV for composition: W-3.5 wt%Ni-1.5 wt%Fe-25 wt%Cu, respectively. Although the additions of Ni and Fe made the Cu matrix network structure have a uniform distribution, it led to a decrease in the electron transfer ability of the alloy, and thus, there was a decrease in electrical conductivity.

Fabrication and characterization of W/Cu/Ni-based high specific gravity alloy with Zr and Ti combined addition

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Microstructure and Properties of In-Situ TiC Reinforced Copper Nanocomposites Fabricated Via Long-Term Ball Milling and Hot Pressing

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Fabrication and Characterization of Tungsten Heavy Alloys with High W Content by Powder Metallurgy

Enhanced Mechanical and Electrical Properties of CuCrZr-WC Alloy Prepared by Mechanical Alloying and Spark Plasma Sintering

Preparation and properties of W-30 wt% Cu alloy with the additions of Ni and Fe elements

Improving mechanical properties of W-Ni 3 Al alloy through Zr element addition: Solid-solution and oxide particle strengthening

Fabrication and Properties of Nano-TiCx/Cu-Cr-Zr Alloy Composites

Fabrication of W-Cu/Lu2O3 Composites with High Strength and Electrical Conductivity Prepared by Electroless Plating and Powder Metallurgy

Effect of Silver Element on Microstructure and Properties of W-30Cu/TiC Composites

Microstructure and properties of a novel ultra-high strength, high elasticity and high plasticity Cu–20Ni–20Mn-0.3Nb-0.3Cr-0.1Zr alloy

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

Novel low temperature derived W f /W-ZrC-Cu composites by reactive infiltration with enhanced mechanical and thermal physical properties

Fabrication of nanocrystalline and ultra-hard tungsten alloy by dual particles dispersion strengthening

Composition design, microstructure, and mechanical properties of novel Ti–Co–Ni–Zr complex concentrated alloys

Preparation of in situ TiC@TiN core–shell and Ti2N–Al4C3 nanoparticles and their effects on Al–Zn–Mg–Cu alloy

WC-Co-TiNbZr composite with simultaneously high hardness and fracture toughness

Fabrication of W–Cu/CeO2 Composites with Excellent Electric Conductivity and High Strength Prepared from Copper-Coated Tungsten and Ceria Powders

Performance of a Hierarchically Nanostructured W–Cu Composite Produced via Mediating Phase Separation

Effects of Ti Addition on Microstructure, Mechanical Properties and Corrosion Resistance of the Cu-Zn-Ni Alloy