Abstract:Abstract Copper (Cu)-matrix composites combine the high electrical and thermal conductivities of Cu with the enhanced wear resistance and strength of the reinforcement material, and are therefore widely used for electrical contact applications in a diverse range of fields. In the current study, tungsten-reinforced copper (W—Cu) composite powders are fabricated using a novel electroless Cu plating process in which the homogeneity of the powder mixture is improved via the use of an ultrasonic agitation technique. The volume content of the tungsten particle reinforcement in the composite specimens is 3, 6, and 12 per cent, respectively, and standard powder metallurgical techniques are then applied to produce the final composite powders. The mechanical and electrical properties of the composite powders are evaluated at room temperature and at temperatures ranging from 100 to 300 °C. Fracture surfaces of the composite samples are ana-lysed using scanning electron microscopy. The results show that the mechanical properties of the W—Cu composite samples are significantly better than those of pure Cu specimens, particularly at higher temperatures. Furthermore, the addition of 3 vol% W particles to the W—Cu composite is found to yield a reduction of not more than 2 per cent in the electrical conductivity of the composite sample compared to that of a pure Cu specimen. Overall, the results indicate that the optimal mechanical and electrical properties are obtained by mixing pure Cu powder with 3 vol% of Cu-plated W particles with a mean dimension of 1 μm.

Multilayered W-Cu composites with enhanced strength, electrical conductivity and wear resistance

Long-term Ball Milling and Hot Pressing of In-Situ Nanoscale Tungsten Carbides Reinforced Copper Composite and Its Characterization

Recent Advances in W–Cu Composites: A Review on the Fabrication, Application, Property, Densification, and Strengthening Mechanism

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

High-temperature mechanical and electrical properties of W-particle-reinforced Cu-matrix composites from improved electroless plated powders

Insight into the Microstructure and Tensile Behavior of the W–Cu Composite Reinforced with Tungsten Fibers and Particulates

Fabrication of W-Cu/Lu2O3 Composites with High Strength and Electrical Conductivity Prepared by Electroless Plating and Powder Metallurgy

Freeze-casted tungsten skeleton reinforced copper matrix composites

Improving comprehensive performance of copper matrix composite by spray pyrolysis fabricated CNT/W reinforcement

Simultaneous enhancement of strength and conductivity via self-assembled lamellar architecture

Fabrication of W–Cu/CeO2 Composites with Excellent Electric Conductivity and High Strength Prepared from Copper-Coated Tungsten and Ceria Powders

Achieving high ductility in layered carbon nanotube/copper composite prepared by composite electrodeposition

Effect of Grain Refinement on the Comprehensive Mechanical Performance of W–Cu Composites

Multiphase strengthening mechanism of Cu-Y2O3/W composites prepared by mechanical alloying

Excellent wear resistance of multicomponent nanocrystalline W‒Cu based composite

Strengthening Mechanisms and Research Progress in the W/Cu Interfaces

Fabrication and microstructure of W-Cu composites prepared from Ag-coated Cu powders by electroless plating

Fabrication, mechanical and thermal properties of tungsten-copper coated graphite flakes reinforced copper matrix composites

Facile fabrication of layer-structured graphene/copper composite with enhanced electrical and mechanical properties

Engineering performance of tungsten network reinforced copper matrix composites synthesized by selective laser melting and infiltration

Microstructure and Properties of W Cu Composites with Low Copper Content at Different Sintering Temperatures