Abstract:WC-Co cemented carbides are widely used in the fields of military, aerospace, mining and cutting industry etc. In this paper, a new two-step method for the preparation of WC-Co cemented carbides was proposed. First, the mixture of yellow tungsten trioxide (WO3) and cobaltic oxide (Co2O3) were reduced by carbon black to remove all the oxygen. Then, the carbothermic reduction products were precisely mixed with an appropriate amount of carbon black to directly prepare WC-Co cemented carbides. The effects of C/WO3 ratio on the phase composition, morphological evolution, particle size and mechanical properties of products are investigated. The experimental results revealed that when the C/WO3 molar ratio was above 2.7, all oxygen in the raw material mixture were removed by carbon black and a mixture of W2C and η-phase were obtained after the first step of carbothermic reduction at 1150 °C for 2 h; then, the mixture of carbothermic reduction product and an appropriate content of carbon black was compacted, and the green compact was first carbonized at 1200 °C for 2 h and then sintered at 1450 °C for 4 h to prepare cemented carbides. With the increase of C/WO3 ratio at the first stage, the content of η-phase with a low melting point increased, which resulted in the large grain size of WC in the finally prepared cemented carbide. Compared with the traditional method of preparing cemented carbides, the cemented carbides prepared by the current method showed a higher hardness and toughness. Furthermore, the addition of a proper content of the VC in the second stage can significantly inhibit the grain growth of WC and further increase the hardness of cemented carbides.

Effect of (Ti,W)C/TaC addition on the early oxidation behavior of surface layer of WC-Co cemented carbides

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Influences of Cr contents on oxidation behavior of WC-Co-Ni-Cr cemented carbides at 900 °C

Mechanism of the early stages of oxidation of WC–Co cemented carbides

Effect of Y2O3 Addition on High-Temperature Oxidation of Binderless Tungsten Carbide

High temperature fracture mechanism of ultrafine WC-Co cemented carbides containing (Ti,W)C

Effects of Cr3C2, VC, and TaC on Microstructure, WC Morphology and Mechanical Properties of Ultrafine WC–10 wt. % Co Cemented Carbides

Oxidation behavior of functionally graded cemented carbides with CoNiFeCr multi-principal-element alloy binder

Selective oxidation induced wear degradation in cemented carbides

Influence of Carbon Contents on the Structure and Tribocorrosion Properties of Tisicn Coatings on Ti6al4v

Microstructural characteristics and wear-resistant mechanisms of WC-TiC-co coatings with varying TiC contents

Mechanisms responsible for enhancing low‐temperature oxidation resistance of nonstoichiometric (Zr,Ti)C

Improvement of high-temperature oxidation resistance of WC–Co–Ni alloy by Cr3C2–CeO2–WS2 mixed additives and its mechanism

Effect of tungsten carbide content on the tribological behavior of TiB2–TiC-based cermets

Oxidation Behavior of Tungsten Carbide-6% Cobalt Cemented Carbide

High-temperature wear and cyclic oxidation behavior of (Ti, W)C reinforced stainless steel coating deposited by PTA on a plain carbon steel

Study on the oxidation of WC-Co cemented carbide under different conditions

Oxidation behavior of non-stoichiometric (Zr,Hf,Ti)Cx carbide solid solution powders in air

Oxidation behavior of the CVD-Al2O3 coatings on tungsten substrate at 1000 °C

A short and facile process to synthesize WC-Co cemented carbides

Effect of TiC addition on the microstructure and properties of Ni3Ta–TaC reinforced Ni-based wear-resistant coating