Abstract:Titanium alloys are known for being difficult to machine. Within the groups of Ti alloys, the machinability is reduced when going from the α-alloys, to α + β, and finally to near-β or β-alloys. Uncoated cemented carbide is traditionally used for machining these alloys and finding a suitable coating to improve the performance is a challenge due to the high strength of Ti alloys and the high chemical reactivity of Ti with tool and coating materials at the temperatures achieved during cutting. The PVD applied Ti x Al 1-x N (x = 0.4–0.7) is generally recommended for machining Ti alloys and a top layer of NbN has shown promising performance in milling applications. This study systematically explores the wear mechanisms of either uncoated WC-12%Co or its Ti 0.45 Al 0.55 N-NbN coated version in the milling of Ti alloys ranging from near-α (Ti-6Al-2Sn-4Zr-2Mo), α + β (Ti-6Al-2Sn-4Zr-6Mo), and near-β (Ti-5Al-5Mo-5 V-3Cr) alloys. The wear evolution is explored by studying as-worn tools and their cross-section using SEM-XEDS and EBSD after having reached 10%, 30%, 50%, and 100% of the full tool life at a flank wear criterion VB = 200 μm. The coating is removed within seconds of engagement and fails by cracking within the bulk and PVD droplet defects can initiate such cracks. Diffusional dissolution of the coating may be active on a minor scale, but the rapid mechanical failure shows the need for a more robust coating formulation. Exposed cemented carbide is worn at varying intensities when machining the Ti alloys. The highest wear rate is achieved in milling α + β Ti-6246, followed by a moderate wear rate in near-β Ti-5553, and with a slower wear rate in milling near-α Ti-6242 which is explained varying intensities in oxidation wear, diffusional dissolution, and mechanical cracking. Diffusional loss of C gives rounder WC grains and remaining W at the interface is removed by the chip flow. Diffusional loss of Co gives reduced grain bonding and loss of the dampening effect that leads to fractures in WC grains. Specifically in milling α + β Ti-6246 and in minor scale in near-α Ti-6242, there is formation of CoWO 4 ceramic present several μm into the tool and its formation is facilitated by the oxidation of binder with resolved W. Fractures within the CoWO 4 explains the high wear rate. Cracks also propagate in binder regions initiated from weakened interface regions due to diffusional loss of C and Co.

Oxidation behavior of the CVD-Al2O3 coatings on tungsten substrate at 1000 °C

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Effect of High Temperature Annealing on the Microstructure and Thermal Shock Resistance of Tungsten Coatings Grown by Chemical Vapor Deposition

High-Performance Al–Si Coatings Toward Enhancing Oxidation Resistance of Tungsten by Halide-Activated Pack Cementation

High Temperature Oxidation Behaviors of Al/Cr Composite Coating on Ti2AlNb Alloy

Microstructure and high-temperature oxidation behavior of Ti3AlC 2/W composites

Oxidation behavior at 1100 °C of NiCrAlY coatings deposited by various PVD techniques

Oxidation Resistance of Quintuple Ti-Al-Si-C-N Coatings and Associated Mechanism

Oxidative Ablation Behavior of W‐Coated C/C Composites Prepared by Chemical Vapor Deposition with Heat Treatment

Oxidation behavior of ceramic coatings on Ti–6Al–4V by micro-plasma oxidation

Oxidative ablation behavior of W‐coated C/C composites prepared by CVD with heat‐treatment

The oxidation behaviors of TiB1.73, Al0.59Ti0.41N, and TiB1.73/Al0.59Ti0.41N coatings deposited by high-power impulse magnetron sputtering method

Oxidation Behavior of Aluminide Coatings on Cobalt-Based Superalloys by a Vapor Phase Aluminizing Process

Structure and High-Temperature Oxidation Performance of Si-Co Diffusion Coatings Prepared on a TiAl-Nb Alloy

Effect of (Ti,W)C/TaC addition on the early oxidation behavior of surface layer of WC-Co cemented carbides

Oxidation characteristics of gamma-TiAl-8Nb coated with a CrAlYN/CrN nanoscale multilayer coating

On the wear mechanisms of uncoated and coated carbide tools in milling titanium alloys

Oxidation Resistance of （ti,al,cr）n Coatings at 800 ℃

Oxidation resistance of (Ti,Al,Cr)N coatings at 800 ℃

On wear of TiAlN coated tools with and without NbN overlayer in machining titanium alloys

Isothermal oxidation resistance and microstructure evolution of VPS-TiAlCrY coating on TiAl single crystals at 1100-1200 o C