Microstructure and high-temperature oxidation behavior of Ti3AlC 2/W composites

Bai Cui,Eugenio Zapata-Solvas,Michael John Reece,ChangAn Wang,William Lee
DOI: https://doi.org/10.1111/jace.12095
IF: 4.186
2013-01-01
Journal of the American Ceramic Society
Abstract:Using spark plasma sintering, Ti3AlC2/W composites were prepared at 1300 degrees C. They contained core-shell microstructures in which a TixW1x shell surrounded a W core, in a Ti3AlC2 matrix. The composite hardness increased with W addition, and the hardening effect is likely achieved by the TixW1x interfacial layer providing strong bonding between Ti3AlC2 and W, and by the presence of hard W. Microstructural development during high-temperature oxidation of Ti3AlC2/W composites involves -Al2O3 and rutile (TiO2) formation 1000 degrees C and Al2TiO5 formation at similar to 1400 degrees C while tungsten oxides appear to have volatilized above 800 degrees C. Likely due to exaggerated, secondary grain growth of TiO2-doped alumina and the effect of W addition, fine (<1m) Al2O3 grains formed dense, anisomorphic laths on Ti3AlC2/5wt%W surfaces 1200 degrees C and coarsened to large (>5m), dense, TiO2-doped Al2O3 clusters on Ti3AlC2/10wt%W surfaces 1400 degrees C. W potentially affects the oxidation behavior of Ti3AlC2/W composites beneficially by causing formation of TixW1x thus altering the defect structure of Ti3AlC2, resulting in Al having a higher activity and by changing the scale morphology by forming dense Al2O3 laths in a thinner oxide coating, and detrimentally through release of volatile tungsten oxides generating cavities in the oxide scale. For Ti3AlC2/5wt%W oxidation, the former beneficial effects appear to dominate over the latter detrimental effect.
What problem does this paper attempt to address?