Abstract:The impact damage evolution of thermally sprayed WC-Ni coatings was studied under 1-8000 impacts at a fixed load of 10 kN order. With increasing impact number, the accumulative damages of coatings evolve by in-sequence occurrence of WC spallation, coating cracking, and mixed coating/interface cracking accompanied with crack length and width growing. To comprehensively evaluate the coated component performance by observed accumulative damages as the failure criteria, a critical impact number N c with critical load L c is proposed for the onsets of different cracking features. The impact resistance is quantified, by N c ( L cc ) for onset of the coating cracking, and N c ( L cm ) for the mixed coating/interface cracking. A subclassification is identified as N c ( L cm1 ) and N c ( L cm2 ), respectively, for sequential occurrence of the isolated interface cracking and the propagated interface cracking of the penetrated from the coating surface. As the coating thickness is increased from 50 to 200 μm, the impact resistance under a load of 11.1 kN is correspondingly improved with N c ( L cc ) prolonged from 3000 to 4500, and N c ( L cm1 ) from 4500 to 5000. In particular, N c ( L cm2 ) is 6000 for the 50 μm coating, but no N c ( L cm2 ) failure for the 200 μm coating up to 8000 impacts. The impact stress field analysis reveals reduced amplitudes of cyclic surface tensile stress and interface shear stress for the thicker coating, together with the interface shear stress shifting from a tensile-compressive alternating mode to a monotonous tensile one. The impact resistance of coated components under repetitive impacts is interpreted on thermodynamics where the thicker coatings mitigate impact mechanical energy dissipation of plastic strain energy in both coating and steel substrate, and accommodate larger reversible elastic strain energy during the periodic loading-unloading of impact cycles.

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Effect of High Temperature Annealing on the Microstructure and Thermal Shock Resistance of Tungsten Coatings Grown by Chemical Vapor Deposition

Experimental and Numerical Simulations of ELM-like Transient Damage Behaviors to Different Grade Tungsten and Tungsten Alloys

Tungsten Joining with Copper Alloy and Its High Heat Load Performance

HIGH HEAT LOAD PROPERTIES OF W/Cu FUNCTIONALLY GRADED MATERIALS

Thermal Performance and Microstructure of Vacuum Plasma Sprayed Tungsten Coatings under Cyclic Heat Load

Surface Cracking of Tungsten-Vanadium Alloys under Transient Heat Loads

Microstructure of Chemical Vapor Transport Deposition Single Crystal Tungsten Coating Working at 1600°C

Thermal shock behaviors and failure mechanisms of EB-PVD thermal barrier coatings using radiant heating

High-temperature tensile and thermal shock characterization of low-temperature rolled tungsten

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Recent progress of thick tungsten coating prepared by chemical vapor deposition as the plasma-facing material

Surface Damage During Transient Thermal Load of 50% Thickness Reduced W-2% (vol.) Y2O3 Sheet with Different Recrystallization Volume Fraction

Microstructure Evolutions of the W–TiC Composite Conducted by Dual-Effects from Thermal Shock and He-ion Irradiation

Surface Damage and Microstructure Evolution of Yttria Particle-Reinforced Tungsten Plate During Transient Laser Thermal Shock

Oxidation behavior of the CVD-Al2O3 coatings on tungsten substrate at 1000 °C

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient

Accumulative Damages of Thermally Sprayed Cemented Carbide Coatings Under Repetitive Heavy-Load Impacts

Failure Mechanism of EB-PVD Thermal Barrier Coatings under the Synergistic Effect of Thermal Shock and CMAS Corrosion