Abstract:This paper looks at the tribology of thermal sprayed WC–Co based coatings and covers the high energy air–sand erosion resistance and slurry jet impingement erosion performance, dry and wet sliding tribology of thermal spray WC–Co based coatings as well as the abrasion and abrasion–corrosion of these coatings. The tribological and tribo-corrosion performance of the coatings will be related to their mechanical and corrosion properties as well as deposition parameters, microstructure and actual composition. For example, the anisotropic microstructure of thermally sprayed WC–Co–Cr coatings, in particular the low fracture toughness in a direction parallel to the substrate, has been observed to affect the nature of crack formation under 200μJ air–solid particle erosion conditions. Voids and occasionally other microstructural features (i.e., cobalt lakes, splat boundaries, interfacial inclusions) in the coating act as crack initiation sites. The erosion rate was dominated by cracks within 5μm of the surface and was relatively insensitive to total length of cracks, showing a near-surface damage front controls the erosion rate and this region is coincident with the region of maximum shear stress induced by erodent impacts. Optimisation of the deposition parameters of HVOF 86WC–10Co–4Cr coatings show an improvement in erosion resistance of more than 50% over the conventional D-gun applied coating of identical nominal composition. The variation in the slurry erosion performance of the thermally sprayed coatings is also linked to directional fracture toughness and crack propagation paths which are influenced by the presence of pores, inhomogeneous carbide distributions and substrate grit blast remnants. The influence of slurry jet angle is more pronounced under 0.4μJ energy conditions where maximum erosion occurred at 90° and the minimum at 30° in contrast to 7μJ slurry erosion rates which were independent of jet angle. This reflects the lower levels of fluctuating stresses imparted to the coating during low energy slurry impacts leading to the impact angle having a greater effect on sub critical crack growth rate than for higher energy conditions.The abrasion resistance of these coatings was found comparable to sintered cermets of the same composition. The synergistic effects between micro and macro abrasion and corrosion for detonation gun (D-gun) sprayed WC–10Co–4Cr coatings are shown to be significant and depend on the environment. The size effect of the abradant relative to the microstructure and splat size is important as well as the propensity for the various phases to passivate to control corrosion levels. Comparisons between exposed and freshly polished coating surfaces in strong NaOH solutions (pH 11) show that significantly lower wear rates were seen for the exposed surface due to a negative wear–corrosion synergy due to selective phase removal and the effects of localised passivation.Dry and wet sliding wear resistance of these coatings is shown to be high (wear rates of 10−16–10−18m3/Nm) with modest coefficient of friction levels between 0.2 and 0.5. The presence of oxides on the binder phases appears to influence the friction and wear levels. Wear appears to be by carbide ejection and/or by tribo-chemical processes.

Accumulative Damages of Thermally Sprayed Cemented Carbide Coatings Under Repetitive Heavy-Load Impacts

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Atomistic Investigation of Titanium Carbide Ti8C5 under Impact Loading

Design for Manufacturing of Cemented Carbide Coated Components Toward High Wear and Impact Resistance Performance

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Optimizing Wear Resistance and Tensile Strength of Nickel-Based Coatings through Tungsten Carbide Reinforcement

Study of the Fatigue Wear Behaviors of a Tungsten Carbide Diamond-Like Carbon Coating on 316L Stainless Steel

Micro-scale impact resistance of coatings on hardened tool steel and cemented carbide

Effect of WC on microstructure, molten pool and properties of Ni based coatings by multi-layer laser cladding

Enhanced Fracture Toughness of WC-CoCr Thermally Sprayed Coatings by the Addition of NiCrFeSiBC and Mo and Its Influence on Sliding Wear Behavior

Impact-sliding wear properties of PVD CrN and WC/C coatings

Tribology of thermal sprayed WC–Co coatings

Impact Evaluation Of Plasma Spray Coatings

High-Temperature Wear Behavior and Mechanisms of Self-Healing NiCrAlY-Cr3C2-Ti2SnC Coating Prepared by Atmospheric Plasma Spraying

Erosion Resistance Of Ni-Wc Self-Fluxing Alloy Coating At High Temperature

Friction and wear behavior of Ni-based alloy coatings with different amount of WC–TiC ceramic particles

Impact Wear of the Protective Cr3C2-Based HVOF-Sprayed Coatings

Three-Body Abrasive Wear Behavior of WC-10Cr3C2-12Ni Coating for Ball Mill Liner Application

Erosion Behavior of Cold-Sprayed Coatings Made of CoCrFeMnNi HEA and Tungsten Carbide Nanoparticles in a Nickel Matrix

Estimation of fatigue life of TiN coatings using cyclic micro-impact testing