Abstract:The impact damage evolution of thermally sprayed WC-Ni coatings was studied under 1-8000 impacts at a fixed load of 10 kN order. With increasing impact number, the accumulative damages of coatings evolve by in-sequence occurrence of WC spallation, coating cracking, and mixed coating/interface cracking accompanied with crack length and width growing. To comprehensively evaluate the coated component performance by observed accumulative damages as the failure criteria, a critical impact number N c with critical load L c is proposed for the onsets of different cracking features. The impact resistance is quantified, by N c ( L cc ) for onset of the coating cracking, and N c ( L cm ) for the mixed coating/interface cracking. A subclassification is identified as N c ( L cm1 ) and N c ( L cm2 ), respectively, for sequential occurrence of the isolated interface cracking and the propagated interface cracking of the penetrated from the coating surface. As the coating thickness is increased from 50 to 200 μm, the impact resistance under a load of 11.1 kN is correspondingly improved with N c ( L cc ) prolonged from 3000 to 4500, and N c ( L cm1 ) from 4500 to 5000. In particular, N c ( L cm2 ) is 6000 for the 50 μm coating, but no N c ( L cm2 ) failure for the 200 μm coating up to 8000 impacts. The impact stress field analysis reveals reduced amplitudes of cyclic surface tensile stress and interface shear stress for the thicker coating, together with the interface shear stress shifting from a tensile-compressive alternating mode to a monotonous tensile one. The impact resistance of coated components under repetitive impacts is interpreted on thermodynamics where the thicker coatings mitigate impact mechanical energy dissipation of plastic strain energy in both coating and steel substrate, and accommodate larger reversible elastic strain energy during the periodic loading-unloading of impact cycles.

Impact Evaluation Of Plasma Spray Coatings

Frequency Spectrum Analysis of Impact Response for Plasma Sprayed Coatings

Response Frequency Spectrum Analysis for Impact Behavior Assessment of Surface Materials

Particle Impact Damage and Point Load-Induced Fracture Behavior in Zirconia Plasma Spray Coating Film

Investigation of stress field and failure mode of plasma sprayed Al2O3–13%TiO2 coatings under thermal shock

Wear performance of the plasma sprayed fine WC-Co composite powders coatings

Three Body Abrasive Wear Characteristics of Plasma Sprayed Conventional and Nanostructured Al2O3-13%TiO2 Coatings

The influence of powder types and plasma spray conditions on abrasive wear of nanostructured and conventional Al2O3TiO2 coatings

Thermal Shock Properties and Failure Mechanism of Plasma Sprayed Al2O3/TiO2 Nanocomposite Coatings

The dependency of microstructure and properties of nanostructured coatings on plasma spray conditions

The Influence of Powder Types and Plasma Spray Conditions on Abrasive Wear of Nanostructured and Conventional Al2o3/Tio2 Coatings

Study on Wear Resistance and Spraying Process of Nano-ZrO2 Powder Plasma Spraying Coating

Study on Properties of Coatings Prepared by Supersonic Plasma Spraying with Three Kinds of WC-12Co Powder

Accumulative Damages of Thermally Sprayed Cemented Carbide Coatings Under Repetitive Heavy-Load Impacts

Thermal Shock Behavior of Nanostructured and Conventional Al2O3/13 Wt%tio2 Coatings Fabricated by Plasma Spraying

The Inspection Of The Sliding Surface And Subsurface Of Plasma-Sprayed Ceramic Coatings Using Scanning Acoustic Microscopy

Effect of Spraying Power on the Microstructure and Mechanical Properties of Supersonic Plasma-Sprayed Ni-based Alloy Coatings

Experimental Study on Water Droplet Erosion Resistance of Coatings (ni60 and WC-17Co) Sprayed by APS and HVOF

The Effect of Plasma Spray Parameters on the Quality of Al-Ni Coatings

Abrasive wear characteristics of plasma sprayed nanostructured alumina/titania coatings

Fabrication and Evaluation of Plasma Sprayed Nanostructured Alumina–titania Coatings with Superior Properties