Microstructure and wear behavior of WC-reinforced AlCoCrFeNiSi high entropy alloy coatings prepared by high-velocity arc spraying
Zaharaddeen Aminu Bello,Min Kang,Joseph Ndiithi Ndumia,Chunlei Geng,Abdulaziz Nuhu Jibril,Zehao Liu
DOI: https://doi.org/10.1016/j.surfcoat.2024.131421
IF: 4.865
2024-10-04
Surface and Coatings Technology
Abstract:In this study, AlCoCrFeNiSi/WC (WC from 0 to 40 wt%) high entropy alloys (HEAs) coatings were deposited on Q235 steel substrates using high-velocity arc spraying technique. The coatings' phases, microstructure, microhardness, nano-hardness, wear properties, and the mechanisms of wear were examined. The results have shown that the WC reinforced HEA had faced-centered cubic, body-centered cubic solid solution and carbide phases, while faced-centered cubic solution and Cr 3 Si, Al 2 O 3 phase were observed in AlCoCrFeNiSi coating. The coatings possess a dense, lamellar structure and strong adhesion to the substrates. With the addition of reinforced particles, the porosity of the coatings initially decreases and then increases. The average microhardness of the coatings is significantly improved as WC content increased, reaching a maximum of 530 HV 0.1 . The ratio of nano-hardness to reduced elastic modulus rises as more WC is introduced. The coatings with the WC particles exhibit good wear resistance with the optimum wear rate at WC content of 40 wt%. Under the same conditions, the coating with 40 wt% of WC displayed the lowest wear rate, which decreased by 60.5 % compared to the AlCoCrFeNiSi coating. The AlCoCrFeNiSi coating experienced a mix of adhesive, abrasive, oxidative, and fatigue wear mechanisms. The wear mechanism changed to more abrasive, adhesive, and oxidative in the reinforced coatings. The load-bearing capacity and secondary phase strengthening effects of WC reduce the wear rate of the coatings.
physics, applied,materials science, coatings & films