Abstract:In order to improve the wear resistance and service life of die steel, Ni-based alloy coatings with different amount of WC–TiC ceramic particles were fabricated on the substrate of Cr12MoV die steel by laser. Scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction were used to analyze the microstructures and phases of four coatings. The results show that four coatings have a good metallurgical bonding with the substrate and no crack and porosity on the surface. The reinforced phases were mainly γ~(Fe, Ni), Cr23C6, WC and Cr2Ti. The microstructure was mainly columnar dendrite, cellular dendrite and equiaxed crystal. When the mass fraction of WC particles was 40%, equiaxed crystal appeared in the coating. The WC and TiC particles were evenly distributed among γ~(Fe, Ni) and Cr23C6 phases. With the increase of WC mass fraction, the values of microhardness increased significantly, which were 680.5, 704.3, 752.6 and 806.4 HV0.5, respectively. The coating of 40% WC particles had the maximum microhardness (806.4 HV0.5). The wear volumes of four coatings were 0.47, 0.44, 0.26 and 0.40 mm3, respectively. With the increase of WC content, the wear resistance increased firstly and then decreased. When the mass fraction of WC particles was 30%, the coating had the minimum wear volume (0.26 mm3) and obtained the best wear resistance. It can be seen that the proper amount of WC and TiC ceramic particles enhanced the wear resistance of laser cladding coating.

What problem does this paper attempt to address?

The paper primarily discusses the preparation of Ni-based alloy coatings with varying WC (tungsten carbide) contents on the Cr12MoV die steel substrate using laser cladding technology to improve the wear resistance and service life of the die steel. In the study, by changing the proportion of WC ceramic particles (from 10% to 40%) and maintaining a constant 10% TiC (titanium carbide) content in all samples, the changes in the microstructure, phase composition, hardness, and wear performance of the coatings were investigated. Specifically, the key findings in the paper include: 1. **Good metallurgical bonding between the coating and the substrate**: All four coatings formed a good metallurgical bond with the Cr12MoV substrate, with no cracks or pores on the surface. 2. **Formation of reinforcing phases**: Multiple reinforcing phases were formed in the coatings, including c*(Fe, Ni), Cr_23C6, WC, and Cr_2Ti. WC and TiC particles were evenly distributed among the c*(Fe, Ni) and Cr_23C6 phases. 3. **Microstructural changes**: As the WC content increased, the microstructure of the coatings transitioned from columnar dendrites and cellular dendrites to equiaxed grains. When the WC mass fraction reached 40%, equiaxed grains appeared in the coating, which inhibited crystal growth and led to an increase in hardness. 4. **Hardness and wear performance**: With the increase in WC content, the microhardness of the coatings significantly improved, with the maximum hardness occurring in the coating with 40% WC content, reaching 806.4 HV_0.5, which is approximately 3.5 times that of the Cr12MoV substrate. However, the wear volume of the coatings first decreased and then increased, with the minimum wear volume (0.26 mm^3) and the best wear resistance observed when the WC mass fraction was 30%. 5. **Conclusion**: An appropriate content of WC and TiC ceramic particles can significantly improve the wear resistance of laser cladded coatings, while an excess of WC can weaken the bond between the hard particles and the c*(Fe, Ni) solid solution, reducing the wear resistance of the coating. In summary, by optimizing the content of WC and TiC particles, the wear resistance and hardness of the Cr12MoV die steel surface can be effectively enhanced, thereby extending its service life. This research provides a theoretical basis for the surface modification of Cr12MoV die steel.

Friction and wear behavior of Ni-based alloy coatings with different amount of WC–TiC ceramic particles

Microstructure and Wear Resistance of Ni-WC-TiC Alloy Coating Fabricated by Laser

Effect of Ultra-fine WC Particles on Microstructural Evolution and Wear Behavior of Ni-Based Nano-CeO2 Coatings Produced by Laser

Microstructure and High-Temperature Tribological Properties of Laser-Cladded WC10Co4Cr–xTi2AlC Coatings

Microstructure and Wear Resistance of AlCoCrFeNi-WC/TiC Composite Coating by Laser Cladding

Effect of Ceramic Particles on Ni-Based Alloy Coating Fabricated via Laser Technology

Microstructure and wear resistance of laser cladding FeNiCrMo-WC composite coating

Tribological Performance and Wear Mechanism of Laser Cladded NiCrAl-WC Coatings at High-Temperature

Influence of WC ceramic particles on structures and properties of laser cladding Ni50-WC coatings

Microstructure and tribological properties of laser cladded TiC reinforced WC-10Co4Cr coatings at 500 °C

Study on the friction and wear performance of laser cladding WC-TiC/Ni60 coating on the working face of shield bobbing cutter

Optimizing Wear Resistance and Tensile Strength of Nickel-Based Coatings through Tungsten Carbide Reinforcement

Effect of WC-12Co on the mechanical and wear performance of laser melting deposition nickel-based alloy

Effect of in-situ grown TiC on microstructure and tribological performance of laser cladded NiCrAl-40 %WC coating by addition of Ti

Effect of WC on microstructure, molten pool and properties of Ni based coatings by multi-layer laser cladding

Microstructure and wear resistance of laser cladding WC particles reinforced composite coatings

Study Of Wear And Corrosion Resistances Of Ni60-Wc + Tic Composite Coating

Study of Microstructure and Properties of Laser Cladding Ni60-WC + TiC Composite Coating

Microstructure and Wear Behavior of Ti-xFe-SiC In Situ Composite Ceramic Coatings on TC4 Substrate from Laser Cladding

Microstructure and properties of TiC-enhanced CrMnFeCoNi high-entropy alloy coatings prepared by laser cladding

Effect of WC–Co addition on tribological and cracking behavior of laser cladded Fe-based amorphous/crystalline composite coatings