Abstract:While the addition of WC increases the hardness and wear resistance of coatings, an excessive WC content can also induce crack initiation and propagation, increasing brittleness and leading to premature failure. Therefore, in this study, WC particles were incorporated into nickel-based coatings by plasma-arc surfacing to optimize their content and distribution, balancing their tensile properties and wear resistance. The coatings were comprehensively evaluated through microstructural analysis, hardness testing, wear resistance assessment, and tensile testing. The results show that as the mass fraction of WC increased from 45% to 65%, the increase in carbon significantly promoted the formation of M7C3, M6C, and M23C6 carbides and suppressed the formation of the γ-phase. The microstructural analysis showed that the content of massive carbides increased significantly with the increasing WC content, and the XPS analysis further confirmed that the changes in the WC and Cr7C3 phases were particularly pronounced in the high-WC coating. The 65% WC coating showed higher hardness (a 232 increase in HV1.0), a lower and more stable coefficient of friction (0.42), and better wear resistance than the 45% WC coating, with a wear rate of 3.329 × 10−6 mm3/(N·m)−1, which was 3.709 × 10−6 mm3/(N·m)−1 lower than that of the 45% WC coating. The conventional tensile test results show that the maximum stress and strain of the 45% WC coating were 71% and 36% higher than those of the 65% WC coating, respectively. In addition, the 45% WC coating exhibited better ductility and quasi-cleavage characteristics, whereas the 65% WC coating showed typical brittle cracking behavior. The results of the field tensile tests also showed that the fracture time of the 65% WC coating was 27 s shorter than that of the 45% WC coating. Overall, the 45% WC coating had a good combination of strength and toughness.

Microstructural characteristics and wear-resistant mechanisms of WC-TiC-co coatings with varying TiC contents

Microstructure and Tribological Properties of WC/Ni-MoS2 Titanium-Based Composite Coating on TC4

Effect of WC addition on microstructure and properties of laser melting deposited Ti6Al4V

Microstructure and tribological properties of laser cladded TiC reinforced WC-10Co4Cr coatings at 500 °C

Microstructure and High-Temperature Tribological Properties of Laser-Cladded WC10Co4Cr–xTi2AlC Coatings

Microstructure and sliding wear properties of WC-10Co-4Cr coatings on the inner surface of TC4 slender tube by HVOF

Influence of Carbon Contents on the Structure and Tribocorrosion Properties of Tisicn Coatings on Ti6al4v

Effects of WC mass fraction on microstructure and tribological behavior of plasma sprayed FeMnCoCr–WC coatings

Optimizing Wear Resistance and Tensile Strength of Nickel-Based Coatings through Tungsten Carbide Reinforcement

Cold-sprayed Cu Matrix Composite Coatings with Core-Shell Structured Co@WC Reinforcements on Q235 Steel

Effects of Y2O3 Content on the Microstructure and Tribological Properties of WC-Reinforced Ti-Based Coatings on TC4 Surfaces

Microstructural evolution and wear characteristics of laser-clad CoCrFeNiMn high-entropy alloy coatings incorporating tungsten carbide

Promising WC-30WB-10Co Cemented Carbide Coating with Improved Density and Hardness Deposited by High Velocity Oxy-Fuel Spraying: Microstructure and Mechanical Properties

High-temperature wear and cyclic oxidation behavior of (Ti, W)C reinforced stainless steel coating deposited by PTA on a plain carbon steel

Friction and wear behavior of Ni-based alloy coatings with different amount of WC–TiC ceramic particles

Microstructure evolution and tribological behavior of laser cladded Al 1.8 CrCuFeNi 2 /WC composite coatings on Ti-6Al-4 V

Preparation of in-situ synthesized TiC/AlSi30Cu5 coating by high velocity oxy-fuel (HVOF) spraying: Microstructure evolution, mechanical properties, and tribological behavior

Effect of in-situ grown TiC on microstructure and tribological performance of laser cladded NiCrAl-40 %WC coating by addition of Ti

Corrosion and wear resistant WC17Co-TC4 composite coatings with fully dense microstructure enabled by in-situ forging of the large-sized WC17Co particles in cold spray

Microstructure characterization and wear performance of WC-10Co/Ti-6Al-4V coating fabricated via electron beam cladding

Evolution of microstructure and wear mechanism in laser clad Al0.5CoCrFeNiSi0.5Tix coatings in response to the Ti addition