Abstract:WC/Fe matrix composites with mass fractions of 30–50 wt% were prepared by gravity casting and infiltration, and the phase composition, microstructure, friction and wear properties of the composites were studied. In addition, the mechanism of the effect of the change of WC mass fraction on the structural evolution and wear properties of the composites was particularly investigated. The results show that the composites are mainly composed of WC, α-Fe, W 2 C, Fe 6 W 6 C, and M 7 C 3 phases. With the increase of WC mass fraction, the microstructure of the composite shows different results, WC particles start to dissolve under the action of high temperature melt, W elements solidly dissolve into the matrix and precipitate into fishbone structure carbide. As the content of WC particles in the prefabricated body increases, the C atoms around the WC particles react with the dissolved W atoms, and due to the cooling of the metal liquid, the energy transferred between the WC and the metal liquid does not make it melt completely before solidification occurs, and the metallurgical reaction between the WC particles and the substrate occurs and produces a dense interface. The WC/Fe matrix composites showed a trend of increasing and then decreasing with the increase of WC content and friction coefficients of 0.36, 0.52, and 0.26. The wear rates were 1.52(mm 3 /N-m) × 10 −5 , 1.24(mm 3 /N-m) × 10 −5 , and 1.57(mm 3 /N-m) × 10 −5 , which showed the opposite trend with the friction coefficients, and the wear rates were compared with the morphology. When the composite was added with 40% WC, the wear rate increased by 27% compared with other parameters. It shows that it has good wear resistance.

Effects of WC mass fraction on microstructure and tribological behavior of plasma sprayed FeMnCoCr–WC coatings

Microstructure and Properties of FeMnCrAl/Ni Coated WC Coatings Deposited by High Velocity Arc Spraying

Effects Of Wc Crystal Characteristics On Microstructure And Mechanical Property Of Hvof-Sprayed Wc-Cocr Coatings

Study on Microstructure and Thermal Fatigue of FeMnCrAl/WC Coatings

Research on microstructure, mechanical property and wear mechanism of AlCoCrFeNi/WC composite coating fabricated by HVOF

Wear Properties of Plasma Transferred Arc Fe-based Coatings Reinforced by Spherical WC Particles

Effect of WC-10Co-4Cr Reinforcement Amount on Wear and Corrosion Resistance of Fe-Based Amorphous Coatings

Wear performance of the plasma sprayed fine WC-Co composite powders coatings

Effect of WC mass fraction on the microstructure and frictional wear properties of WC/Fe matrix composites

Microstructure and High-Temperature Tribological Properties of Laser-Cladded WC10Co4Cr–xTi2AlC Coatings

Microstructure and tribological properties of laser cladded TiC reinforced WC-10Co4Cr coatings at 500 °C

Microstructural characteristics and wear-resistant mechanisms of WC-TiC-co coatings with varying TiC contents

Comparative tribological study of air plasma sprayed WC–12%Co coating versus conventional hard chromium electrodeposit

Microstructure and mechanical property of high velocity oxy-fuel sprayed WC-Cr3C2-Ni coatings

Oxidation corrosion wear and lubricating mechanisms of WC particles reinforced FeCoCrNiMn high - entropy alloys coatings

Microstructure and Tribological Properties of WC/Ni-MoS2 Titanium-Based Composite Coating on TC4

Effect of Cobalt and Chromium Content on Microstructure and Properties of WC-Co-Cr Coatings Prepared by High-Velocity Oxy-Fuel Spraying

Microstructure and wear behavior of FeCoNiCrMn high entropy alloy coating deposited by plasma spraying

Tribological Performance and Wear Mechanism of Laser Cladded NiCrAl-WC Coatings at High-Temperature

Effect of WC addition on microstructure and properties of laser melting deposited Ti6Al4V

Microstructural evolution and wear characteristics of laser-clad CoCrFeNiMn high-entropy alloy coatings incorporating tungsten carbide