Abstract:This paper looks at the tribology of thermal sprayed WC–Co based coatings and covers the high energy air–sand erosion resistance and slurry jet impingement erosion performance, dry and wet sliding tribology of thermal spray WC–Co based coatings as well as the abrasion and abrasion–corrosion of these coatings. The tribological and tribo-corrosion performance of the coatings will be related to their mechanical and corrosion properties as well as deposition parameters, microstructure and actual composition. For example, the anisotropic microstructure of thermally sprayed WC–Co–Cr coatings, in particular the low fracture toughness in a direction parallel to the substrate, has been observed to affect the nature of crack formation under 200μJ air–solid particle erosion conditions. Voids and occasionally other microstructural features (i.e., cobalt lakes, splat boundaries, interfacial inclusions) in the coating act as crack initiation sites. The erosion rate was dominated by cracks within 5μm of the surface and was relatively insensitive to total length of cracks, showing a near-surface damage front controls the erosion rate and this region is coincident with the region of maximum shear stress induced by erodent impacts. Optimisation of the deposition parameters of HVOF 86WC–10Co–4Cr coatings show an improvement in erosion resistance of more than 50% over the conventional D-gun applied coating of identical nominal composition. The variation in the slurry erosion performance of the thermally sprayed coatings is also linked to directional fracture toughness and crack propagation paths which are influenced by the presence of pores, inhomogeneous carbide distributions and substrate grit blast remnants. The influence of slurry jet angle is more pronounced under 0.4μJ energy conditions where maximum erosion occurred at 90° and the minimum at 30° in contrast to 7μJ slurry erosion rates which were independent of jet angle. This reflects the lower levels of fluctuating stresses imparted to the coating during low energy slurry impacts leading to the impact angle having a greater effect on sub critical crack growth rate than for higher energy conditions.The abrasion resistance of these coatings was found comparable to sintered cermets of the same composition. The synergistic effects between micro and macro abrasion and corrosion for detonation gun (D-gun) sprayed WC–10Co–4Cr coatings are shown to be significant and depend on the environment. The size effect of the abradant relative to the microstructure and splat size is important as well as the propensity for the various phases to passivate to control corrosion levels. Comparisons between exposed and freshly polished coating surfaces in strong NaOH solutions (pH 11) show that significantly lower wear rates were seen for the exposed surface due to a negative wear–corrosion synergy due to selective phase removal and the effects of localised passivation.Dry and wet sliding wear resistance of these coatings is shown to be high (wear rates of 10−16–10−18m3/Nm) with modest coefficient of friction levels between 0.2 and 0.5. The presence of oxides on the binder phases appears to influence the friction and wear levels. Wear appears to be by carbide ejection and/or by tribo-chemical processes.

Comparative tribological study of air plasma sprayed WC–12%Co coating versus conventional hard chromium electrodeposit

Comparative Study of Thermally Sprayed Coatings Under Different Types of Wear Conditions for Hard Chromium Replacement

Effects of WC mass fraction on microstructure and tribological behavior of plasma sprayed FeMnCoCr–WC coatings

High temperature tribological behavior of atmospheric plasma-sprayed CoCrFeNiW0.3 + 5 at% C high-entropy alloy coating

Microstructure and Tribological Properties of FeCoCrNi High-Entropy Alloy Coatings Fabricated by Atmospheric Plasma Spraying

Comparison of the Mechanical and Electrochemical Properties of WC-25Co Coatings Obtained by High Velocity Oxy-Fuel and Cold Gas Spraying

Tribology of thermal sprayed WC–Co coatings

Comparative Micro-Scale Abrasive Wear Testing of Thermally Sprayed and Hard Chromium Coatings

Tribological Behavior of Various Plasma-Sprayed Ceramic Coatings

Effect of Cobalt and Chromium Content on Microstructure and Properties of WC-Co-Cr Coatings Prepared by High-Velocity Oxy-Fuel Spraying

High-temperature tribological behavior of thermally-treated supersonic plasma sprayed Cr3C2-NiCr coatings

Promising WC-30WB-10Co Cemented Carbide Coating with Improved Density and Hardness Deposited by High Velocity Oxy-Fuel Spraying: Microstructure and Mechanical Properties

Microstructure and Tribology Behaviors of In-Situ WC/Fe Carbide Coating Fabricated by Plasma Transferred Arc Metallurgic Reaction

Wear properties of WC–Co and WC–CoCr coatings applied by HVOF technique on different steel substrates

Investigations on Tribological and Microstructure Characteristics of WC-12Co/FeNiCrMo Composite Coating by HVOF Process

Oxidation corrosion wear and lubricating mechanisms of WC particles reinforced FeCoCrNiMn high - entropy alloys coatings

Effects of WC on the Microstructure, Wear and Corrosion Resistance of Laser-Deposited CoCrFeNi High Entropy Alloy Coatings

The Dry Sliding Wear Behavior of HVOF-Sprayed WC: Metal Composite Coatings

High Temperature Oxidation and Tribological Behavior of Cr3C2-25CoNiCrAlY and Cr3C2-25NiCr Coatings Prepared by AC-HVAF

Thick WC-12Co Coatings on Bearing Steel Fabricated by Low-Temperature High-Velocity Fuel Spray Process

Investigation of Novel Nano-carbide WC/CoCr Coatings Applied by HVAF