Comparative Study of Multilayer Hard Coatings Deposited on WC-Co Hardmetals

Mateja Šnajdar,Danko Ćorić,Matija Sakoman
DOI: https://doi.org/10.3390/coatings14060674
IF: 3.236
2024-05-27
Coatings
Abstract:This paper examines the impact of a multilayered gradient coating, applied via plasma-activated chemical vapor deposition (PACVD), on the structural and mechanical attributes of nanostructured WC-Co cemented carbides. WC-Co samples containing 5 and 15 wt.% Co were synthesized through a hot isostatic pressing (HIP) process using nanoparticle powders and coated with two distinct multilayer coatings: titanium nitride (TiN) and titanium carbonitride (TiCN). Nanosized grain formation without microstructural defects of the substrates, prior to coating, was confirmed by magnetic saturation and coercivity testing, microstructural analysis, and field emission scanning electron microscope (FESEM). Nanoindentation, fracture toughness and hardness testing were conducted for uncoated samples. After coatings deposition, characterizations including microscopy, surface roughness determination, adhesion testing, coating thickness measurement, and microhardness examination were conducted. The impact of deposited coatings on wear resistance of produced hardmetals was analyzed via scratch test and dry sliding wear test. Samples with higher Co content exhibited improved adhesion, facilitating surface cleaning and activation before coating. TiN and TiCN coatings demonstrated similar roughness on substrates of identical composition, suggesting Co content's minimal influence on layer growth. Results of the mechanical tests showed higher microhardness, higher elastic modulus, better adhesion, and overall superior tribological properties of the TiCN coating.
materials science, multidisciplinary, coatings & films,physics, applied
What problem does this paper attempt to address?
The aim of this paper is to address the application of multilayer gradient coatings (specifically TiN and TiCN coatings) on nanostructured WC-Co hard alloys using plasma-activated chemical vapor deposition (PACVD) technology to enhance their mechanical and tribological properties. Specifically, the study focuses on the following aspects: 1. **Improving Surface Performance**: Although WC-Co hard alloys possess excellent hardness, thermal stability, and wear resistance, they are prone to surface damage and wear under harsh conditions. Therefore, advanced coating technologies need to be developed to enhance their performance and durability. 2. **Advantages of PACVD Technology**: Compared to traditional chemical vapor deposition (CVD) and physical vapor deposition (PVD), PACVD can operate at lower temperatures, avoiding the formation of undesirable eta phases and reducing the need for sample rotation. This makes PACVD an ideal choice for coating nanostructured hard alloys. 3. **Coating Characteristics Evaluation**: By applying TiN and TiCN coatings to WC-Co substrates with different Co contents, the study investigates the impact of the coatings on the microstructure of the substrate materials, including improvements in hardness, elastic modulus, adhesion, and overall tribological performance. 4. **Optimizing Coating Process**: By precisely controlling parameters during the coating process, such as temperature, gas flow, and voltage, the quality and performance of the coatings are ensured to reach optimal conditions. 5. **Experimental Validation**: Through a series of experimental tests (such as nanoindentation, fracture toughness, hardness tests, etc.), it is verified that TiCN coatings exhibit higher microhardness, better adhesion, and superior overall tribological performance compared to TiN coatings. In summary, the main objective of this study is to improve the mechanical properties and wear resistance of WC-Co hard alloys by enhancing coating technology and optimizing process parameters, thereby extending tool life and reducing costs.