Abstract:In this study, we investigated the effects of nanostructured composite powders (WC-Ni), nickel binder content, and sintering techniques on the morphology and mechanical properties of tungsten carbide. An alternative low-temperature gas-solid reaction route with a short reaction time was employed to produce nanostructured composite powders with 5 and 15 wt% Ni. The powders were consolidated using spark plasma sintering (SPS) and conventional vacuum furnace sintering at temperatures of 1350 °C and 1450 °C. The composite powders were characterized using scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and particle size measurements. The expansion/contraction of the compacted nanocomposite powders was studied through dilatometric analysis. The composite powders exhibited a uniform distribution of Ni, in both compositions. For the WC-5 wt% Ni nanocomposite powders, the average crystallite sizes for WC and Ni were 41.6 nm and 46.2 nm, respectively. While, for the WC-15 wt% Ni nanocomposite, the crystallite sizes for WC and Ni were 45.6 and 38.4 nm. The sintered composites were evaluated through XRD, SEM, measurements of density and Vickers hardness. The enhanced sinterability of the nanostructured powders enabled their consolidation into (WC-Ni) hard metal with densities approaching the theoretical relative density of 96.07 %, even with low binder content (5 wt% Ni). This is attributed to the uniform distribution of Ni and an extensive Ni-WC interface present prior to sintering. The SPS process at 1350 °C produced sintered bodies (WC-5 wt% Ni and WC-15 wt% Ni) with higher Vickers hardness (2322 HV and 1512 HV, respectively) and superior microstructural quality compared to samples produced by conventional vacuum furnace techniques. These results demonstrated that the mechanical properties of the system WC-Ni processed by SPS are superior to those obtained by vacuum furnace. Therefore, WC-Ni hard metals processed by this approach is a promising alternative to conventional hard metals (WC-Co) for a wide range of applications.

Tribological Properties of Coatings Applied on Near-Nano and Nanostructured WC-Co Hardmetals by Using Plasma-Assisted Chemical Vapour Deposition Technique

Two-Layer Nanocomposite TiC-Based Coatings Produced by a Combination of Pulsed Cathodic Arc Evaporation and Vacuum Electro-Spark Alloying

Comparative Study of Multilayer Hard Coatings Deposited on WC-Co Hardmetals

Analysis of Different Complex Multilayer PACVD Coatings on Nanostructured WC-Co Cemented Carbide

Influence of nano-sized WC addition on the microstructure, residual stress, and tribological properties of WC-Co HVAF-sprayed coatings

Investigation of Novel Nano-carbide WC/CoCr Coatings Applied by HVAF

Microstructure and Tribological Properties of HVOF-Sprayed Nanostructured WC-12Co/Fe3O4 Coatings

Effect of Particle and Carbide Grain Sizes on a HVOAF WC-Co-Cr Coating for the Future Application on Internal Surfaces: Microstructure and Wear

Improved tribological performance and enhanced tensile adhesive strength of micro- to near-nanocrystalline WC-17 wt. %Co coatings sprayed using HVOF

Investigations on Tribological and Microstructure Characteristics of WC-12Co/FeNiCrMo Composite Coating by HVOF Process

Enhanced properties of hard metal WC-Ni processed from nanostructured powders

Comparative tribological study of air plasma sprayed WC–12%Co coating versus conventional hard chromium electrodeposit

Spark Plasma Sintering of Fine-Grained WC-Co Composites

Comparative Study of Thermally Sprayed Coatings Under Different Types of Wear Conditions for Hard Chromium Replacement

Tribological and Micromechanical Properties of the Nanostructured Carbonitride/Nitride Coatings of Transition Metals Alloyed by Hf and Nb

The Hardfacing Properties of the Nickel-based Coating Deposited by the PTA Process with the Addition of WC Nano-particles: Wear Investigation

Influence of WC Particle Size on the Mechanical Properties and Residual Stress of HVOF Thermally Sprayed WC–10Co–4Cr Coatings

Microstructure and Properties Characterization of WC-Co-Cr Thermal Spray Coatings

Microstructure and tribological properties of CrVN thin film coated WC‐Co tool after boriding process

Wear properties of WC–Co and WC–CoCr coatings applied by HVOF technique on different steel substrates

Microstructural and Tribological Resistance of Flame-Sprayed CoMoCrSi/WC-CrC-Ni and CoMoCrSi/WC-12Co Composite Coatings Remelted by Microwave Energy