Abstract:The deposition of ternary nitrides with the incorporation of carbon atoms into its structure has demonstrated to be a promising approach in the pursuit of wear-resistant and self-lubricating coatings. Firstly, both TiAlN and TiAlCN monolayers were deposited using direct current magnetron sputtering (DCMS) and high-power impulse magnetron sputtering (HiPIMS) onto quenched and tempered AISI H11 tool steel to be used as references. Acetylene was used as a carbon precursor, producing DCMS and HiPIMS TiAlCN coatings with 9.0 and 21.7 at.% C, respectively.Subsequently, TiAlN/TiAlCN multilayers of various designs were also developed as follows: 5×[10/500], 5×[50/500] and 5×[100/500] nm. Residual stresses of the coating systems were determined by X-ray radiation utilising an ETA-diffractometer with a Cu-Kα radiation source applying the sin2ψ method. Additionally, residual stresses depth gradients of the substrate before and after the deposition of the coatings were determined in a LEDDI 8-circle diffractometer equipped with a W-X-ray tube and operated in the energy-dispersive mode of diffraction. Great reduction of the compressive residual stresses in the coatings was observed after the introduction of carbon into the TiAlN coating structure, shifting from −1047 ± 149 to −307 ± 211 MPa for the DCMS and from −7035 ± 1361 to +989 ± 187 MPa for the HiPIMS coatings. In the multilayer coatings, compressive residual stresses increase along with the increment of the TiAlN interlayer. Additionally, residual stresses of the substrate in the near-surface are dragged from low compressive stresses (−218 ± 61) to tensile stresses in the range of 1000 to 2000 MPa for all the DCMS/substrate systems, a behaviour only presented in HiPIMS by the TiAlN monolayer. Wear coefficients of all the evaluated HiPIMS systems are notoriously lower than their DCMS counterparts. Compared to TiAlN, TiAlCN HiPIMS presented a lower coefficient of friction but a higher wear coefficient, which in turn was not reduced by the introduction of the multilayer systems. Finally, Scratch test and Rockwell C adhesion tests have shown higher adhesion of DCMS coatings than HiPIMS coatings, and a detriment of the monolayers adhesion by the implementation of TiAlN/TiAlCN multilayer systems. The understanding of the residual stresses, both in the coating and in the substrate, and the way they affect the tribomechanical performance of the system coating/substrate continues to be of great importance, especially for coatings deposited by new technologies such as HiPIMS and self-lubricating coatings.

Comparative studies on corrosion and tribological performance of multilayer hard coatings grown on WC-Co hardmetals

Comparative Study of Multilayer Hard Coatings Deposited on WC-Co Hardmetals

Influence of multi-interfacial structure on mechanical and tribological properties of TiSiN/Ag multilayer coatings

Improvement of the tribological behavior of TiN/CrN multilayer coatings by modulation wavelength variation

Contrast Role of Third Body Layer and Hard Abrasives in the Wear Process of a TiAlSiN Hardness-Modulated Multilayer Coating: A Case Study on the Effect of Normal Load and Velocity

Mechanical properties, thermal stability and oxidation resistance of TiN/CrN multilayer coatings

Growth, mechanical properties, and tribological performance of TiAlN/NbN and NbN/TiAlN bilayer coatings

The impact of Ni and Mo on growth-morphology and mechanical properties of arc evaporated Ti-Cr-N hard coatings

The influence of multilayer structure on mechanical behavior of TiN/TiAlSiN multilayer coating

Study of the Performance of Laser Melting Wear-Resistant Coatings on TC4 Titanium Alloy Surfaces

Residual stresses and tribomechanical behaviour of TiAlN and TiAlCN monolayer and multilayer coatings by DCMS and HiPIMS

Microstructure and High-Temperature Tribological Properties of Laser-Cladded WC10Co4Cr–xTi2AlC Coatings

Corrosion and wear behavior of TiN PVD coated 304 stainless-steel

Microstructure and Tribological Properties of Multilayered ZrCrW(C)N Coatings Fabricated by Cathodic Vacuum-Arc Deposition

Nanoindentation and Tribological Behavior of TiN-TiCN-TiAlN Multilayer Coatings on AISI D3 Tool Steel

Fabrication and Performance of TiN/TiAlN Nanometer Modulated Coatings

Tribological behaviour of TiAlN and AlCrN coatings on stainless steel

Long-term tribocorrosion resistance and failure tolerable of multilayer carbon-based coatings

Improved adhesion and erosion wear performance of CrSiN/Cr multi-layer coatings on Ti alloy by inserting ductile Cr layers

Comparative investigation and characterization of the nano-mechanical and tribological behavior of RF magnetron sputtered TiN, CrN, and TiB2 coating on Ti6Al4V alloy

Influence of Bilayer Thickness on Mechanical and Tribological Properties of (Ti-Al)N/MoN Nanostructured Hard Coatings Deposited by Cathodic Arc Ion Plating