Improved adhesion and erosion wear performance of CrSiN/Cr multi-layer coatings on Ti alloy by inserting ductile Cr layers

Fei Cai,Jiamin Zhang,Jianming Wang,Jun Zheng,Qimin Wang,Shihong Zhang

DOI: https://doi.org/10.1016/j.triboint.2020.106657

IF: 5.62

2021-01-01

Tribology International

Abstract:<p>Cr/CrSiN multi-layer coatings with various multi-layer structures were fabricated on titanium alloy (TC4) by ion-plating technology. Microstructures, adhesion, wear and friction, and erosion wear performance were investigated. The results showed the Cr/CrSiN-10 multi-layer coating exhibited higher adhesive strength <strong><u>(HF1)</u></strong>, and low friction coefficient <strong><u>(0.44)</u></strong> and wear rate (<strong><u>4.1 × 10</u></strong>^{<strong>−10</strong>} <strong>mm</strong>^{<strong>3</strong>} <strong>N</strong>^{<strong>−1</strong>}<strong><u>·m</u></strong>^{<strong>−1</strong>}). This improved wear resistance of the Cr/CrSiN multi-layer coating (Cr/CrSiN-10) was due to the reduced probability of coating peels. The Cr/CrSiN-10 multi-layer coating also exhibited lower erosion wear rate (<strong><u>0.05</u> μm s</strong>^{<strong>−1</strong>}<strong><u>) compared with Cr/CrSiN-1 coating</u></strong> (<strong><u>0.15</u> μm s</strong>^{<strong>−1</strong>}<strong><u>)</u></strong>. It is proposed that the improved erosion wear resistance of Cr/CrSiN multi-layer coating arises from the fact that the erosion cracks were intercepted and captured by the ductile Cr layers and the multi-layer structures.</p>

engineering, mechanical