Microstructure and properties of multilayer WC-40Co coating on Ti-6Al-4V by electron beam cladding
Wenqin Wang,Shiqi Zhang,Sheng Xiao,Yutaka S. Sato,De Wang,Yong Liu,Donglei Liu,Qiang Hu
DOI: https://doi.org/10.1016/j.matchar.2021.111585
IF: 4.537
2022-01-01
Materials Characterization
Abstract:Single, double, and triple-layer WC-40Co coatings were prepared by electron beam (EB) cladding to improve the wear resistance of Ti-6Al-4V. The microstructure, microhardness, wear resistance, and corrosion resistance of the coatings were investigated. The results demonstrated that the three types of coatings consisted of β (Ti, W), TiCo, (Ti, W) C1-X, (W, Ti) C1-X, and a small amount of Ti2Co. The core/shell structure of (W, Ti) C1-X/ (Ti, W) C1-X was observed by TEM, and the phase interfaces were studied. The hardness and wear resistance of triple-layer coating was the highest, and its wear resistance was improved by 11.5 times that of the substrate. The wear mechanisms of the substrate, single- and double-layer coating was oxidative and abrasive wear, while the triple-layer coating exhibited abrasive wear. The corrosion resistance of the single- and double-layer coatings was better than that of the substrate; however, the triple-layer coating surface was significantly damaged owing to the cracks.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing