Abstract:SiC layer was prepared in an industrial scale spout fluidized bed by chemical vapor deposition. The density of SiC coating was about 3.18 g/cm(3). High temperature oxidation experiments were carried out at different temperatures from 800 to 1600 degrees C. The microstructure and composition were characterized using different methods, including mass change weighing, XRD, EDS and SEM. It was found that the weight gain of SiC coating layer was not obvious below 1200 degrees C, and subsequent mass gain gradually increased with increasing temperature, reaching 10% at 1600 degrees C. High-magnification SEM results show that the oxidation began from the surface and gradually formed punctate distribution of the oxide. Small crystal structure (similar to micron) of the SiC surface was very clear at 1000 degrees C, and this crystal structure disappeared gradually at high temperatures, forming oxides of Si in the SiC surface. There was a stacking fault stress due to the different thermal expansion coefficients and elastic modulus of SiC and Si oxides, leading to the gradual formation of cracks around the punctates. With increasing temperature, the crack further increased the oxidation rate of SiC, and finally the formed Si oxides layer fell off from the particles. It can be seen clearly that the layer was peeling when the temperature was increased to 1400 degrees C. Increasing the temperature to 1600 degrees C, the SiC coating was oxidized completely into a honeycomb structure, with obvious sintering of SiC. XRD analysis shows that there was a growing SiO2 peaks from 1400 degrees C, indicating that surface oxidation was significant. EDS results shows that the oxygen content in the coating surface gradually increased with increasing temperature. Semi-quantitative analysis shows that the surface was close to SiO2 at 1600 degrees C.

Cl 2 corrosion resistance of SiC coatings with different morphologies

Corrosion of SiC-coated graphite susceptor by NH3 and Cl2

The corrosion behavior of CVD SiC coatings on SiCf/SiC composites in a simulated molten salt reactors environment

High Temperature Oxidation Behavior of SiC Coating Materials

The corrosion resistance mechanisms of the cr-coated SiC in molten Na2SO4 salt: Strengthened boundaries and protective scales

Analysis of oxidation behavior of laser cladding SiC-Ti based composite strengthening coating

SiC Performance of Coated Fuel Particles under High-Temperature Atmosphere of Air

Microstructure and Ablation Properties of SiC/ZrB2–SiC/ZrB2/SiC Multilayer Coating on Graphite

Understanding the Corrosion and Tribological Behaviors of CrSiN Coatings with Various Si Contents in HCl Solution

Microstructure and Corrosion Resistance of SiC Nanoparticles Reinforced Ceramic Composite Coating on Mg-Li Based Composite by Micro-Arc Oxidation

Effect of deposition temperature on the corrosion behavior of CVD SiC coatings on SiCf/SiC composites under simulated PWR conditions

Thermal cycling behavior of La2Zr2O7/Yb2Si2O7/SiC coated PIP Cf/SiC composites under burner rig tests

Structure and corrosion resistance of SiC thin film coated on NdFeB by magnetron sputtering

Effect of the Incorporation of SiC Nanowire with Double Protective Layers on SiC Coating for C/C Composites

The structure of chemical vapor deposited silicon carbide

Microstructure, Mechanical and Tribological Properties of CrSiC Coatings Sliding Against SiC and Al2O3 Balls in Water

The effect of the SiC content on the high duration erosion behavior of SiC/ZrB2– SiC/ZrB2 functionally gradient coating produced by shielding shrouded plasma spray method

Improved antioxidative and mechanical properties of SiC coated C/C composites via a SiO2-SiC reticulated layer

Investigation of Impact of C/Si Ratio on the Friction and Wear Behavior of Si/SiC Coatings Prepared on C/C-SiC Composites by Slurry Reaction Sintering and Chemical Vapor Infiltration

SiC/MoSi2-SiC-Si Oxidation Protective Coatings for HTR Graphite Spheres with Residual Si Optimized

SiC coating as hydrogen permeation reduction and oxidation resistance for nuclear fuel cladding