Abstract:SiC layer was prepared in an industrial scale spout fluidized bed by chemical vapor deposition. The density of SiC coating was about 3.18 g/cm(3). High temperature oxidation experiments were carried out at different temperatures from 800 to 1600 degrees C. The microstructure and composition were characterized using different methods, including mass change weighing, XRD, EDS and SEM. It was found that the weight gain of SiC coating layer was not obvious below 1200 degrees C, and subsequent mass gain gradually increased with increasing temperature, reaching 10% at 1600 degrees C. High-magnification SEM results show that the oxidation began from the surface and gradually formed punctate distribution of the oxide. Small crystal structure (similar to micron) of the SiC surface was very clear at 1000 degrees C, and this crystal structure disappeared gradually at high temperatures, forming oxides of Si in the SiC surface. There was a stacking fault stress due to the different thermal expansion coefficients and elastic modulus of SiC and Si oxides, leading to the gradual formation of cracks around the punctates. With increasing temperature, the crack further increased the oxidation rate of SiC, and finally the formed Si oxides layer fell off from the particles. It can be seen clearly that the layer was peeling when the temperature was increased to 1400 degrees C. Increasing the temperature to 1600 degrees C, the SiC coating was oxidized completely into a honeycomb structure, with obvious sintering of SiC. XRD analysis shows that there was a growing SiO2 peaks from 1400 degrees C, indicating that surface oxidation was significant. EDS results shows that the oxygen content in the coating surface gradually increased with increasing temperature. Semi-quantitative analysis shows that the surface was close to SiO2 at 1600 degrees C.

Effect of deposition temperature on the corrosion behavior of CVD SiC coatings on SiCf/SiC composites under simulated PWR conditions

The corrosion behavior of CVD SiC coatings on SiCf/SiC composites in a simulated molten salt reactors environment

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Microstructural and mechanical evolution of SiCf/SiC composites in wet oxygen atmosphere above 1000 degrees C

Water vapor corrosion resistance and failure mechanism of SiCf/SiC composites completely coated with plasma sprayed tri-layer EBCs

Wear behavior of SiC nanowire-reinforced SiC coating for C/C composites at elevated temperatures

Influence of SiC Nanowires on the Properties of SiC Coating for C/C Composites Between Room Temperature and 1500°C

Oxidation resistance and thermal shock behavior of tri-layer Si/Si–Yb2SiO5/Yb2SiO5–SiC environmental barrier coatings at 1300 °C

The impact of water and oxygen contents on the corrosion performance of yttrium silicate modified SiC f /SiC composites under high temperature conditions

Hydrothermal Corrosion Behaviors of Constituent Materials of SiC/SiC Composites for LWR Applications

Corrosion behavior of CVI 2D Cf/SiC composites under high temperature burner rig tests

Corrosion Resistance of Ceramics Based on SiC under Hydrothermal Conditions

Investigation of Yb2SiO5/BSAS/Si coating on Cf/SiC composites: processing and steam corrosion behavior

Deposition voltages on the phase evolutions, microstructures, and oxidation behaviors of thermal-resistance Glass-MoSi2-SiC coating

High Temperature Oxidation Behavior of SiC Coating Materials

The Oxidation Behavior and Corrosion Mechanism of SiC Matrix Ceramics in a High Temperature Wet Air Environment

Effect of temperature-dependent nano SiC on the ablation resistance of ZrC coating

Influence of SiC Coatings on the Tribological Behaviors of Graphite for High Temperature Gas-Cooled Reactor

Cyclic oxidation and water vapor corrosion behaviors of multi-layer environmental barrier coatings with HfO2-Si bond coat for SiCf/SiC

Effect of heat treatment on the microstructure and properties of CVD SiC fiber

Comparison of Oxidation Behaviors of 3D C/PyC/SiC and SiC/PyC/SiC Composites in an O2-Ar Atmosphere