Abstract:The near stoichiometric SiC fiber has been reported to play significant roles in the application of aero‐engine field. An in‐depth understanding on the degradation mechanism of the fiber during its corrosion in air and under a simulated aeroengine environment (PH2O: PO2: PAr = 14:8:78 kPa) will shine a light on the performance evaluations of the near stoichiometric SiC fiber‐based materials as well as the development of their potential applications. In this study, .XRD, SEM, and FIB‐TEM were utilized to analyze the mechanical properties and microstructure of the fiber. After oxidation in dry air and Ar‐H2O‐O2 for 1h, respectively the fiber strength retention rate has been found to decreases with the increased oxidation temperature. The raise in oxidation temperature also led to the increasing of the thickness and the crystallization rate of the oxide scale. The most different oxidation behavior of SiC being treated under the simulated environment than in air is the lower oxidation activation energy and the higher crystallization activation energy for cristobalite. Water vapor can promote the oxidation reaction and inhibit the crystallization of cristobalite in the oxide scale. Few significant differences have been observed otherwise in the oxidation process and oxidation chromatography crystallization mechanism of fibers being treated under different conditions.. The increase of oxide layer thickness and the formation of cristobalite impair the structural integrity and compactness of the oxide scale and thus leads to the deterioration of the mechanical properties of SiC fibers. Therefore, it is proposed that oxidation resistance of SiC fiber can be improved by insulating the reaction between the oxidizing agents and the SiC fiber, or by increasing the crystallization temperature of cristobalite in the oxidation process and reducing the crystallization rate. This article is protected by copyright. All rights reserved

The impact of water and oxygen contents on the corrosion performance of yttrium silicate modified SiC f /SiC composites under high temperature conditions

Oxidation behaviors of yttrium silicate modified SiCf/SiC composites in air and water‐oxygen environments

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Y/YbB4-modified SiCf/SiC composites with enhanced water-oxygen corrosion resistance

Recent progress on wet-oxygen corrosion resistance of SiC f /SiC composites

Preparation and properties of SiC/SiC-SiYC with excellent water-oxygen corrosion resistance

Enhanced wet-oxidation resistance of Y2O3 modified SiC ceramics by the formation of Y2Si2O7 protective layer

Corrosion behavior of precracked SiCf/SiC composites under 1200–1300°C Na2SO4‐wet‐oxygen environment

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

Femtosecond laser ablation behavior of SiC/SiC composites in air and water environment

Mechanical Properties and Damage Analysis of SiCf/SiC and SiCf/SiC-EBC Composites in High-Temperature Combustion Gas Environment

Microstructure and water corrosion behavior of (Lu0.2Yb0.2Er0.2Tm0.2Sc0.2)2Si2O7 high-entropy rare-earth disilicate coating for SiC coated C/C composites

Tensile-tensile fatigue behavior of plain-woven SiCf/SiC ceramic matrix composites with differently spaced film cooling holes and environmental barrier coatings in high-temperature water-oxygen environments

The corrosion behavior of CVD SiC coatings on SiCf/SiC composites in a simulated molten salt reactors environment

An analytical model for the high temperature fracture strength of SiC fiber reinforced ceramic matrix composites considering oxidation and residual thermal stresses

Oxidation Behavior of SiCf/SiC Composites Modified by Layered-Y2Si2O7 in Wet Oxygen Environment

Properties evolution and damage mechanism of SiC/SiC composites after thermal shock at 1300 °C

Degradation mechanism of near stoichiometric SiC fibers after air and Ar‐H2O‐O2 corrosion at 1000∼1500°C

Corrosion behavior of CVI 2D Cf/SiC composites under high temperature burner rig tests

High-temperature mechanical properties and oxidation resistance of SiCf/SiC ceramic matrix composites with multi-layer environmental barrier coatings for turbine applications

Failure mechanism of ytterbium silicate/silicon bi-layer environmental barrier coatings on SiCf/SiC composites upon long-time water vapor and oxygen corrosion test