Abstract:SiC layer was prepared in an industrial scale spout fluidized bed by chemical vapor deposition. The density of SiC coating was about 3.18 g/cm(3). High temperature oxidation experiments were carried out at different temperatures from 800 to 1600 degrees C. The microstructure and composition were characterized using different methods, including mass change weighing, XRD, EDS and SEM. It was found that the weight gain of SiC coating layer was not obvious below 1200 degrees C, and subsequent mass gain gradually increased with increasing temperature, reaching 10% at 1600 degrees C. High-magnification SEM results show that the oxidation began from the surface and gradually formed punctate distribution of the oxide. Small crystal structure (similar to micron) of the SiC surface was very clear at 1000 degrees C, and this crystal structure disappeared gradually at high temperatures, forming oxides of Si in the SiC surface. There was a stacking fault stress due to the different thermal expansion coefficients and elastic modulus of SiC and Si oxides, leading to the gradual formation of cracks around the punctates. With increasing temperature, the crack further increased the oxidation rate of SiC, and finally the formed Si oxides layer fell off from the particles. It can be seen clearly that the layer was peeling when the temperature was increased to 1400 degrees C. Increasing the temperature to 1600 degrees C, the SiC coating was oxidized completely into a honeycomb structure, with obvious sintering of SiC. XRD analysis shows that there was a growing SiO2 peaks from 1400 degrees C, indicating that surface oxidation was significant. EDS results shows that the oxygen content in the coating surface gradually increased with increasing temperature. Semi-quantitative analysis shows that the surface was close to SiO2 at 1600 degrees C.

The corrosion behavior of CVD SiC coatings on SiCf/SiC composites in a simulated molten salt reactors environment

Effect of deposition temperature on the corrosion behavior of CVD SiC coatings on SiCf/SiC composites under simulated PWR conditions

The corrosion resistance mechanisms of the cr-coated SiC in molten Na2SO4 salt: Strengthened boundaries and protective scales

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Corrosion of Si, C, and SiC in molten salt

Corrosion behaviors of Ti3SiC2/Cu composites in molten salts

Influence of SiC content in B4C–nSiC composites corrosion in molten FLiNaK salt at 800°C

The impact of water and oxygen contents on the corrosion performance of yttrium silicate modified SiC f /SiC composites under high temperature conditions

Internal Friction Behavior Of C/Sic Composites With Environmental Barrier Coatings In Corrosive Environment

The inhibition of the interaction between CVD SiC and GH3535 alloy in molten LiF-NaF-KF salt by the Li metal

Water vapor corrosion resistance and failure mechanism of SiCf/SiC composites completely coated with plasma sprayed tri-layer EBCs

High Temperature Oxidation Behavior of SiC Coating Materials

Corrosion behavior of precracked SiCf/SiC composites under 1200–1300°C Na2SO4‐wet‐oxygen environment

Cl 2 corrosion resistance of SiC coatings with different morphologies

Corrosion behavior of CVI 2D Cf/SiC composites under high temperature burner rig tests

Corrosion of SiC layers on coated zirconia particles in wet atmosphere

Effects of corrosion in liquid fluoride salt on the tensile strength of domestic SiC fibers

High Temperature Oxidation and Microstructural Evolution of SiC Layer of TRISO Particles in the Presence of NaCl

Corrosion behavior of a wear resistant Co-Mo-Cr-Si alloy in molten fluoride salts

The Effect of Molten Salt Infiltration on 2D SiCf/SiC Composite by Chemical Vapour Infiltration

High-quality SiC-HfC coating with interpenetrating structure based on a two-step low temperature molten salt method