Abstract:Silicon carbide fiber-reinforced silicon carbide ceramic matrix composites（SiCf/SiC） used in aero-engines are damaged or even failed due to the oxidation and corrosion by high-temperature and high-speed combustion gases. In this work，the gas generation device was used to simulate the complex gas environment in the aircraft engine，and the aviation kerosene mixed with liquid oxygen fuel in a certain proportion was ignited to form a high-temperature and high-speed combustion gas to assess the material. The oxidation test for 10 h and thermal shock test for 1000 cycles in combustion gas environment at 1200 ℃ were conducted on SiCf/SiC composites respectively. And the protective effect of environmental barrier coating（EBC）on SiCf/SiC composites was investigated. Uniaxial tensile tests were conducted on SiCf/SiC composites and SiCf/SiC-EBC composites after combustion gas environment assessment，and their fracture and cross-section micro-morphologies were observed by scanning electron microscopy. The results show that no significant oxidation of fibers and interphases is found in SiCf/SiC composites and SiCf/SiC-EBC composites after oxidation for 10 h in combustion gas environment，and their uniaxial tensile strength decreases by less than 2%. After 1000 thermal shock cycles in combustion gas environment，multiple micro-cracks are formed and oxidative corrosion of the interfacial layer occurs inside the SiCf/SiC composites，and the uniaxial tensile strength decreases by 41.3%. The EBC coating can effectively protect the SiCf/SiC composites from oxidation and corrosion of high-temperature gas，and the uniaxial tensile strength of SiCf/SiC-EBC composites decreases by 16.6% after 1000 thermal shock cycles.

Internal Friction Behavior Of C/Sic Composites With Environmental Barrier Coatings In Corrosive Environment

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Internal Friction Behavior Of Sic Ceramics Subjected To Water Vapor Corrosion

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

The Degradation Behavior of C/Sic Composites in Complex Environment

Erosion Behavior of C/SiC Composites in Atomic Oxygen

Internal Friction Mechanisms and Damage Evaluation of Continuous Fiber Reinforced Ceramic Matrix Composites

The corrosion behavior of CVD SiC coatings on SiCf/SiC composites in a simulated molten salt reactors environment

Effect of oxidation on internal friction behavior of C/SiC composites

The impact of water and oxygen contents on the corrosion performance of yttrium silicate modified SiC f /SiC composites under high temperature conditions

Mechanical Properties and Damage Analysis of SiCf/SiC and SiCf/SiC-EBC Composites in High-Temperature Combustion Gas Environment

Microstructure and water corrosion behavior of (Lu0.2Yb0.2Er0.2Tm0.2Sc0.2)2Si2O7 high-entropy rare-earth disilicate coating for SiC coated C/C composites

Fabrication and Water-vapor Corrosion Resistance of Ba<SUB>0.25</SUB>Sr<SUB>0.75</SUB>Al<SUB>2</SUB>Si<SUB>2</SUB>O<SUB>8</SUB> Environmental Barrier Coating

Corrosion behavior of CVI 2D Cf/SiC composites under high temperature burner rig tests

Femtosecond laser ablation behavior of SiC/SiC composites in air and water environment

Investigation of Impact of C/Si Ratio on the Friction and Wear Behavior of Si/SiC Coatings Prepared on C/C-SiC Composites by Slurry Reaction Sintering and Chemical Vapor Infiltration

Fabrication and water-vapor corrosion resistance of Ba0.25Sr0.75 Al2Si2O8 environmental barrier coating

Corrosion Behavior of SiC_w?Al Compoite

Thermal cycling behavior of La2Zr2O7/Yb2Si2O7/SiC coated PIP Cf/SiC composites under burner rig tests

STUDY ON THE CORROSION BEHAVIOR OF Ce CONVERSION COATINGS ON Al6061/SiCp COMPOSITES