Abstract:The use of carbon fiber reinforced plastic (CFRP) is rapidly increasing in aerospace and automobile applications. This is in large part due to the increase strength and modulus of carbon fiber composites compared to other materials such as glass fiber composites. The fiber-matrix interface has been found to be important for high strength in composites. Methods that have been studied and developed to improve interfacial property of composites include: the addition of coupling agents, surface modifications, chemical reaction control and use of nano-fillers for reinforcement. During mechanical loading the shape of carbon fibers, in a composite, is altered with a concomitant change in electrical resistance. Carbon fibers are used as sensing elements in CFRP due to their electrical conductivity. In some more advanced studies, in CRFP, the carbon fibers were used for both strain sensing and damage sensing. The basic theory, in such studies, was that the movement of carbon fiber could be detected by electrical resistance measurement. During loading, the extent of contact between carbon fibers in a CF tow is altered, and the electrical resistance changes from its initial value. In this work, interfacial properties of carbon fiber/polymer composites were evaluated by such electrical resistance measurements. During the wetting process of CF tows by the polymer resins, the change in electrical resistance was recorded and analyzed. The test results for different carbon fibers and polymer resins exhibited different trends. The electrical resistance change was associated with the different wetting conditions, and the interfacial properties were predicted by these electrical resistance measurements. CF tow/epoxy exhibited the poorest carbon tow wettability, the smallest change in resistance and the poorest IFSS and ILSS. For the four systems studied, the relative change in each of these quantities for the materials of a given composite was roughly proportional to the other measured quantities. This may have some very significant practical importance. It may point the way to use quick easy tests to screen and predict other behaviors for composites of different materials and/or processes. Perhaps a simple resistance change test might be used to predict and select good candidate materials, surface processing techniques for high strength composite applications. The proportional relationship between interfacial adhesion and electrical resistance change was obtained by trend fitting line analyses. Ultimately, it was demonstrated that mechanical properties related to interfacial properties might potentially be predicted by electrical resistance measurement and studies of wetting behavior, using empirical formulas and correlations.

Internal Friction Mechanisms and Damage Evaluation of Continuous Fiber Reinforced Ceramic Matrix Composites

Micro Failure Analysis of Fiber Metal Laminates

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

Interfacial Evaluation Of Carbon Frinforced Nano-Composites Using Electrical Resistance Measurement With Wetting Tests

A novel approach based on stress-impedance effect to assess the interfacial properties in fiber-reinforced composites

Internal Friction Behavior Of C/Sic Composites With Environmental Barrier Coatings In Corrosive Environment

Pre-use Interfacial Shear Strength Prediction for Fiber-Reinforced Thermosetting Composites Based on Stress-Impedance Effect of Ferromagnetic Microwires

Effect of interface damage on tensile behavior of fiber-reinforced ceramic-matrix composites after thermal fatigue loading

Failure analysis and experimental study on bolted composite joints based on continuum damage mechanics

Damage and failure analysis of a SiCf/SiC ceramic matrix composite using digital image correlation and acoustic emission

A Monte Carlo simulation of damage and failure process with crack saturation for unidirectional fiber reinforced ceramic composites

New Self-Repairing System for Brittle Matrix Composites Using Corrosion-Induced Intelligent Fiber

Internal Friction Behavior Of Sic Ceramics Subjected To Water Vapor Corrosion

Micromechanical modeling of longitudinal compression behavior and failure mechanism of unidirectional carbon fiber reinforced aluminum composites involving initial fiber misalignment

Micromechanical Modeling of Damage Evolution and Mechanical Behaviors of CF/Al Composites under Transverse and Longitudinal Tensile Loadings.

Proposal of two parameters to evaluate in-situ apparent toughness of interphase in fiber reinforced ceramic matrix composites: Three-dimensional finite element simulations

Interfacial effect on mechanical behaviors of bidirectional-fiber-reinforced composites

On understanding the mechanical properties and damage behavior of C f /SiC composites by indentation method

Effect of fiber roughness on interfacial friction of fiber reinforced ceramic matrix composites

A Quantitative Representation of Damage and Failure Response of 3D Textile SiC/SiC Ceramics Matrix Composites Subjected to Flexural Loading

Comparison of Failure Modes and Damage Mechanisms of CFRP and C/C Composite Joints under Out-of-plane Loading