Abstract:The hot corrosion behaviour of plasma sprayed WC-CoCr coatings on AISI 316L steel substrate is studied in two corrosive salt environments namely 100% Na2SO4 and 75% Na2SO4+25%NaCl at 1000 °C. Also, on WC-CoCr coated AISI 316L steel substrate, a persistent Cr2O3 barrier scale is created employing pre-oxidation at 1200 °C for ten hours with the expectation that it would withstand hot corrosion in a Na2SO4 salt environment at 900 °C. X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), electron micro probe analysis (EPMA) and scanning electron microscopy (SEM) are performed on samples to examine the pre oxidation and hot corrosion characteristics of plasma sprayed WC-CoCr coatings at elevated temperatures. The findings indicate that the presence of both salt environment affects the degradation process of WC-CoCr coatings. The coatings in 100% Na2SO4 and the mixture of 75% Na2SO4+25%NaCl has a weight change of 0.14 mg/cm2 and 0.33 mg/cm2, respectively, after hot corrosion at 1000 °C for 50 cycles. Each cycle includes 1 hour heating in furnace and 20 minutes cooling in ambient air. Corrosion kinetics using thermogravimetric method showed that non-pre-oxidized samples gained 52.5 % more weight and more severely affected by hot corrosion than pre-oxidized ones. During hot corrosion after 2 hours, there was relatively negligible corrosion, but after 4 and 8 hours, deposits of Na2WO4, WO3, Cr2O3 and CoSO4 were produced. Oxides were primarily composed of Cr2O3 and WO3. Cr2O3 and WO3 acted as barriers to the penetration and diffusion of corrosive elements through coatings, which contributed to the hot corrosion resistance in the corrosive area. The hot corrosion deterioration of WC-CoCr coatings may be effectively reduced by introducing pre oxidation. Slower reaction rate of pre oxidized Cr2O3 scale may operate as a barrier which separates hot corrosion by Na2SO4 salt.

The corrosion resistance mechanisms of the cr-coated SiC in molten Na2SO4 salt: Strengthened boundaries and protective scales

The corrosion behavior of CVD SiC coatings on SiCf/SiC composites in a simulated molten salt reactors environment

Effect of Si on the structure and oxidation behavior of Cr-Si coatings on Zry-4 under high temperature steam environment

Tribological and electrochemical properties of Cr–Si–C–N coatings in artificial seawater

Structure, corrosion, and tribological properties of CrSiN coatings with various Si contents in 3.5% NaCl solution

Structure and tribocorrosion behavior of CrMoSiCN nanocomposite coating with low C content in artificial seawater

Understanding the Corrosion and Tribological Behaviors of CrSiN Coatings with Various Si Contents in HCl Solution

Corrosion behavior of precracked SiCf/SiC composites under 1200–1300°C Na2SO4‐wet‐oxygen environment

Structure and corrosion resistance of SiC thin film coated on NdFeB by magnetron sputtering

Influence of SiC content in B4C–nSiC composites corrosion in molten FLiNaK salt at 800°C

Silicon Content Design of CrSiN Films for Good Anti-Corrosion and Anti-Wear Performances in NaOH Solution

Preparation and Corrosion Resistance of Chromium Carbide Coating on Graphite by Disproportionation Reaction in Molten Salt

Microstructure, Mechanical and Tribological Properties of CrSiC Coatings Sliding Against SiC and Al2O3 Balls in Water

Surface morphological studies on hot corrosion behaviour of pre-oxidized plasma sprayed WC-CoCr coating on AISI316L steel in Na 2 SO 4 /NaCl molten salt environment

Corrosion behaviors of Ti3SiC2/Cu composites in molten salts

Evaluation of Corrosion Resistance and Surface Film Analysis after Corrosion Testing of Materials Coated by Chemical Densified Coating Method under Boiling Sulfuric Acid Environment

Exploring the potential for simultaneous enhancement of mechanical, wear and corrosion performance of the CrB2 protective film actuated by soluting Si

Corrosion of SiC layers on coated zirconia particles in wet atmosphere

Fabrication of Co-Based Cladding Layer by Microbeam Plasma and Its Corrosion Mechanism to Molten Salt

Improved antioxidative and mechanical properties of SiC coated C/C composites via a SiO2-SiC reticulated layer

High Temperature Oxidation and Microstructural Evolution of SiC Layer of TRISO Particles in the Presence of NaCl