Tribological behaviors of TiSiC coating in seawater environment
Qi Gao,Jin-long Li,Yu-wei Ye,Xin Jiang,Yue Wang,Jian-min Hu
DOI: https://doi.org/10.1088/2053-1591/aa5233
IF: 2.025
2017-02-07
Materials Research Express
Abstract:The TiSiC coating was deposited on Ti6Al4V substrate material by multi-arc ion plating. Microstructures and mechanical properties of the TiSiC coating were characterized by SEM, XRD, XPS and nanoindentation. The tribological behaviors of the samples were studied in atmosphere, deionized water and seawater by tribometer. The experimental results showed that the coating exhibited a typical amorphous/nanocrystalline structure. The hardness of the TiSiC coating was up to 28 GPa, which was almost 5 times higher than that of the substrate material. The friction coefficients of the TiSiC coating decreased by 2.3%, 25.6%, 27.0%, respectively, compared with the substrate material in atmosphere, deionized water and seawater environments. The wear rates of the TiSiC coating in atmosphere, deionized water and seawater environments were about 1.72 × 10−5 mm3 N−1 m−1, 8.61 × 10−6 mm3 N−1 m−1, 6.78 × 10−6 mm3 N−1 m−1, respectively, which significantly lower than that of the substrate materials, this mainly due to the high hardness and the lubrication of graphite structure sp2C–C phase in the coating.
materials science, multidisciplinary