Structural, mechanical and tribocorrosion performances of CrMoSiN coatings with various Mo contents in artificial seawater

Yongqiang Fu,Fei Zhou,Maoda Zhang,Qianzhi Wang,Zhifeng Zhou

DOI: https://doi.org/10.1016/j.apsusc.2020.146629

IF: 6.7

2020-09-01

Applied Surface Science

Abstract:<p>CrMoSiN coatings containing various molybdenum (Mo) contents were prepared on Si wafers and titanium alloy substrates using unbalanced magnetron sputtering system via adjusting the Mo target current. The microstructures of CrMoSiN coatings were characterized by using X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM) and transmission electron microscope (TEM), respectively. The mechanical properties of coatings were determined using scratch and nano-indentation tests, while the tribocorrosion behavior of coatings sliding against SiC balls in seawater was performed using a linear reciprocating motion of tribometer. The results showed that Cr(Mo)SiN coatings exhibited (200) preferred orientation. By adding the Mo element into CrSiN coating, an substitutional solid solution of (Cr, Mo)N was formed, and the columnar structure became significantly dense. Consequently, the coating surface changed from "fine-dome" like morphology to a relatively flat morphology with "groove-boundaries". The hardness of CrMoSiN coatings accordingly increased to a maximum value of 35.5 GPa at the Mo content of 11.85 at.%. Due to the formation of MoO₃, the tribocorrosion performances of coatings were enhanced.</p>

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films

What problem does this paper attempt to address?

The paper attempts to address the issue that in marine environments, the transmission components of helicopters and ships are continuously subjected to erosion. Therefore, hard coatings with excellent mechanical properties and corrosion resistance are needed to protect metal parts. Specifically, the paper investigates the structure, mechanical properties, and tribocorrosion performance of CrMoSiN coatings with different molybdenum (Mo) contents in artificial seawater. By adjusting the Mo target current, CrMoSiN coatings with different Mo contents were prepared, and their microstructure, mechanical properties, and tribocorrosion behavior were systematically studied.

The main objectives of the paper include:
1. **Optimizing the coating structure**: Investigating the effect of Mo element doping on the microstructure of CrMoSiN coatings, especially the changes in columnar structure.
2. **Improving mechanical properties**: Evaluating the effect of Mo element doping on the hardness and elastic modulus of the coatings, as well as the adhesion strength between the coating and the substrate.
3. **Enhancing tribocorrosion performance**: Analyzing the effect of Mo element doping on the tribocorrosion behavior of the coatings in seawater, particularly under the synergistic action of sliding wear and electrochemical corrosion.

Through these studies, the paper aims to develop a CrMoSiN coating with excellent comprehensive performance to meet the demand for high-performance protective materials in marine environments.