Electrochemical corrosion and tribological properties of CrMoCN coatings sliding against Al2O3 balls in artificial seawater

Maoda Zhang,Fei Zhou,Yongqiang Fu,Qianzhi Wang,Jizhou Kong

DOI: https://doi.org/10.1016/j.surfcoat.2021.127225

IF: 4.865

2021-07-01

Surface and Coatings Technology

Abstract:Due to low density and high specific strength, titanium alloys have been widely used for marine applications. However, the severe wear and corrosion of titanium alloy components is still a problem. To alleviate this problem, protective coatings are applied. In here, the influence of Mo content on the protective performance of CrMoCN coating for Ti-6Al-4V substrate has been investigated. The short- and long-term corrosion resistances of coating in artificial seawater are studied using an electrochemical workstation with three-electrode configuration. The tribological behaviors of CrMoCN coating sliding against Al2O3 ball are evaluated using a ball-on-disk tribo-meter. The results reveal that the CrMoCN coated samples have higher wear- and corrosion-resistances than the bare substrate. The CrMoCN coating with 8.1 at.% Mo displays the highest values of OCP (0.22 V), Rct ((8.639 ± 0.270) × 107 Ω·cm2) and Rp ((3.04 ± 0.24) × 106 Ω·cm2). However, their protective performances are degraded in the long-term, and then the Rp of CrMoCN-2.5 coating continuously decreases from (5.99 ± 0.47) × 105 Ω·cm2 at 7 days to (0.13 ± 0.01) × 105 Ω·cm2 at 35 days. With an increase in the Mo content, the friction coefficient of CrMoCN coating/Al2O3 tribopair decreases from 0.36 to 0.31 while the coating wear rate increases from 4.65 × 10−7 mm3/Nm to 1.01 × 10−6 mm3/Nm.

physics, applied,materials science, coatings & films

What problem does this paper attempt to address?

The paper primarily explores the electrochemical corrosion behavior and tribological performance of CrMoCN coatings in artificial seawater, and investigates the impact of different molybdenum (Mo) contents on the protective performance of the coatings. Specifically:

- **Background and Problem**: Titanium alloys are widely used in marine engineering due to their low density and high specific strength. However, titanium alloy components are prone to severe wear and corrosion in marine environments. To mitigate this issue, researchers have employed protective coatings to enhance their corrosion resistance and wear resistance.
- **Research Object**: The paper studies the short-term and long-term corrosion performance and tribological performance of CrMoCN coatings with different molybdenum contents (ranging from 0.5 A to 3 A) in artificial seawater.
- **Objective**: The goal is to determine the optimal Mo content in CrMoCN coatings through experiments to achieve the best corrosion resistance and wear resistance.

In summary, the paper aims to optimize the corrosion resistance and wear resistance of CrMoCN coatings by varying the molybdenum content, thereby providing an effective protective solution for titanium alloy materials in marine environments.