Abstract:Cr-Si-C-N coatings were deposited on Si(100) wafer and stainless steel 316L by using unbalanced magnetron sputtering via adjusting trimethylsilane (Si(CH3)(3)H, or TMS) flow, and their microstructure and hardness were analyzed by using EDS, SEM, XRD, XPS and nano-indenter. The electrochemical behavior of coatings in seawater were measured by using a CHI660D electrochemical workstation, and the tribological properties of coatings sliding against SiC balls in artificial seawater were investigated by using ball-on-disk tribometers. The results indicated that there were nanocrystallites of Cr(C, N) crystal and amorphous phases such as a-Si3N4 and a-C(a-CNx) in the CrSiCN coatings. With an increase in the TMS flow, the hardness of CrSiCN coatings first increased to the maximum value of 21.3 GPa, and then decreased to 13 GPa. As compared with the CrCN coating, the CrSiCN coatings exhibited a lower friction coefficient. The pitting corrosion only appeared on the wear tracks, and therefore the mechanical wear and wear-accelerated corrosion were the main material deterioration mechanisms in seawater. The impedance modulus and phase value became high in the low frequency range with an increase in the TMS flows. Because the amorphous phase of silicide dispersed in the grains could effectively improve the density of the coatings, thus the coatings deposited at higher TMS flows exhibited better corrosion resistance.

Tribological Properties of Cr(Si)CN Coatings Sliding Against Different Mating Balls in Water

Friction and wear properties of CrSiCN coatings with low carbon content as sliding against SiC and steel balls in water

Microstructure, Mechanical and Tribological Properties of CrSiC Coatings Sliding Against SiC and Al2O3 Balls in Water

Friction and Wear Properties of CrSiCN/SiC Tribopairs in Water Lubrication

Friction and Wear of Self-Mated SiC and Si 3 N 4 in Green Water-Based Lubricant

Tribological Characteristics of Silicon Nitride-chilled Cast Iron with Oil-less Lubrication

Friction and Wear Properties of Si3N4 and SiC Used for Water-Lubricated Sliding Bearings

Tribological and electrochemical properties of Cr–Si–C–N coatings in artificial seawater

Friction and wear performance of CrSiBCN coatings sliding against ceramic and metal counterparts in sea water

Influence of Trimethylsilane Flow on the Microstructure, Mechanical and Tribological Properties of CrSiCN Coatings in Water Lubrication

Microstructure, Mechanical, and Tribological Properties of Cr-Ti-Si-N Coatings

Comparisons of tribological and electrochemical properties of CrSiC and CrSiCN coatings in seawater

Ni/Si3N4 composite coatings and their water lubrication behaviors

Effect of Si Content on the Tribological Properties of Crsin Films in Air and Water Environments

Influence of Carbon Contents on the Structure and Tribocorrosion Properties of Tisicn Coatings on Ti6al4v

Tribological Properties of A‐cnx Coatings Sliding Against SiC Balls in Ethylene Glycol Aqueous Solution

Understanding the Corrosion and Tribological Behaviors of CrSiN Coatings with Various Si Contents in HCl Solution

Electrochemical and Tribological Properties of TiSiCN Coatings in Coolant

Tribological performance of the gradient composite TiAlSiN coating with various friction pairs

Tribological Properties of CrSiN Nanocomposite Films

Tribological Properties of Si3N4-hBN Composite Ceramics Bearing on GCr15 under Seawater Lubrication