Abstract:Silicon carbide fiber-reinforced silicon carbide ceramic matrix composites（SiCf/SiC） used in aero-engines are damaged or even failed due to the oxidation and corrosion by high-temperature and high-speed combustion gases. In this work，the gas generation device was used to simulate the complex gas environment in the aircraft engine，and the aviation kerosene mixed with liquid oxygen fuel in a certain proportion was ignited to form a high-temperature and high-speed combustion gas to assess the material. The oxidation test for 10 h and thermal shock test for 1000 cycles in combustion gas environment at 1200 ℃ were conducted on SiCf/SiC composites respectively. And the protective effect of environmental barrier coating（EBC）on SiCf/SiC composites was investigated. Uniaxial tensile tests were conducted on SiCf/SiC composites and SiCf/SiC-EBC composites after combustion gas environment assessment，and their fracture and cross-section micro-morphologies were observed by scanning electron microscopy. The results show that no significant oxidation of fibers and interphases is found in SiCf/SiC composites and SiCf/SiC-EBC composites after oxidation for 10 h in combustion gas environment，and their uniaxial tensile strength decreases by less than 2%. After 1000 thermal shock cycles in combustion gas environment，multiple micro-cracks are formed and oxidative corrosion of the interfacial layer occurs inside the SiCf/SiC composites，and the uniaxial tensile strength decreases by 41.3%. The EBC coating can effectively protect the SiCf/SiC composites from oxidation and corrosion of high-temperature gas，and the uniaxial tensile strength of SiCf/SiC-EBC composites decreases by 16.6% after 1000 thermal shock cycles.

Recent progress on wet-oxygen corrosion resistance of SiC f /SiC composites

Current research art of rare earth compound modified SiC-CMCs for enhanced wet-oxygen corrosion resistance

The impact of water and oxygen contents on the corrosion performance of yttrium silicate modified SiC f /SiC composites under high temperature conditions

Microstructural and mechanical evolution of SiCf/SiC composites in wet oxygen atmosphere above 1000 degrees C

Enhanced wet-oxidation resistance of Y2O3 modified SiC ceramics by the formation of Y2Si2O7 protective layer

Oxidation behaviors of yttrium silicate modified SiCf/SiC composites in air and water‐oxygen environments

Mechanical Properties and Damage Analysis of SiCf/SiC and SiCf/SiC-EBC Composites in High-Temperature Combustion Gas Environment

Stress-corrosion Behavior of SiCf/SiC under CMAS-wet-oxygen Environments

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

Preparation and properties of SiC/SiC-SiYC with excellent water-oxygen corrosion resistance

Femtosecond laser ablation behavior of SiC/SiC composites in air and water environment

In-situ SiC nanowires reinforced SiC-based multicomponent ceramic coating for protecting SiOC/CF composites

Corrosion behavior of precracked SiCf/SiC composites under 1200–1300°C Na2SO4‐wet‐oxygen environment

Non-Destruction Evaluation Method for Long-Term Oxidation Behavior of SiC/SiC Composites with Different Preforms in Wet Oxygen

Erosion Behavior of C/SiC Composites in Atomic Oxygen

Laser ablation of SiC/SiC ceramic matrix composites: Morphological characterization, component evolution and oxidation mechanisms

Microstructure and mechanical properties of SiC f /SiC composite prepared by chemical vapor infiltration

Improvement of Strength and Oxidation Resistance for SiC/graphite Composites by SiC Coating

Oxidation behavior of SiC‐AlN ceramics exposed to dry oxygen and water oxygen environments at 1100–1300°C

Removal mechanism of SiC/SiC composites by underwater femtosecond laser ablation

Oxidation Behavior of SiCf/SiC Composites Modified by Layered-Y2Si2O7 in Wet Oxygen Environment