Abstract:A tri-layer coating of mullite/Y2Si2O7/(70wt%Y2Si2O7+30wt%Y2SiO5) was prepared on carbon fiber reinforced silicon carbide (C/SiC) composite substrate through dip-coating route for the sake of improving oxidation resistance of C/SiC composites. An Al2O3–SiO2 sol with high solid content was selected as raw material for mullite, and a slurry of Y2O3 powder filled silicone resin was used to synthesize yttrium silicate. The microstructure, phase composition, and oxidation resistance of the coating were investigated. The as-fabricated coating shows high density and favorable bonding to C/SiC substrate. After oxidation at 1400 and 1500 °C for 30 min under static air, the flexural strengths of coated C/SiC composite were both increased by ~30%. The desirable thermal stability and the further densification are responsible for excellent oxidation resistance. With the additional help of compatible thermal expansion coefficients among substrate and sub-layers in coating, the coated composite retained 111.2% of original flexural strength after 12 times of thermal shock in air from 1400 °C to room temperature. The carbothermal reaction at 1600 °C between free carbon in C/SiC substrate and rich SiO2 in mullite resulted in severe frothing and desquamation of coating and obvious degradation in oxidation resistance.

Y/YbB4-modified SiCf/SiC composites with enhanced water-oxygen corrosion resistance

Preparation and properties of SiC/SiC-SiYC with excellent water-oxygen corrosion resistance

The impact of water and oxygen contents on the corrosion performance of yttrium silicate modified SiC f /SiC composites under high temperature conditions

Oxidation behaviors of yttrium silicate modified SiCf/SiC composites in air and water‐oxygen environments

Enhanced wet-oxidation resistance of Y2O3 modified SiC ceramics by the formation of Y2Si2O7 protective layer

Microstructure and Wet-Oxygen Corrosion Behaviors of In-Suit Grown Y3Si2C2 Modified SiCf/SiC Composites

Rare earth monosilicates as oxidation resistant interphase for SiCf/SiC CMC: Investigation of SiCf/Yb2SiO5 model composites

A Novel Strategy to Improve the Corrosion Resistance of Sicf/Sic Composites in High-Temperature Combustion Environments by Cooperation of Self-Healing Sibcn and High-Stability Yb2si2o7

Microstructure and water corrosion behavior of (Lu0.2Yb0.2Er0.2Tm0.2Sc0.2)2Si2O7 high-entropy rare-earth disilicate coating for SiC coated C/C composites

In-situ Grown Y3Si2C2 on RB-SiC Ceramic for Enhanced Wet-Oxygen Corrosion Resistance

Thermal cycling behavior of bi-layer Yb2Si2O7/SiC EBC-coated Cf/SiC composites in burner rig tests

Thermal shock behavior and oxidation resistance of novel SiC nanowires+Si/Yb2Si2O7-Si/Yb2Si2O7 environmental barrier coatings

Failure mechanism of ytterbium silicate/silicon bi-layer environmental barrier coatings on SiCf/SiC composites upon long-time water vapor and oxygen corrosion test

Thermal cycling behavior of La2Zr2O7/Yb2Si2O7/SiC coated PIP Cf/SiC composites under burner rig tests

Preparation and water vapor corrosion behavior of high entropy rare earth disilicate (Y0.25Yb0.25Ho0.25Er0.25) 2Si2O7

Improved water vapor corrosion resistance of SiC bricks via in situ formation of microporous Yb2Si2O7 bonding phase

Investigation of Yb2SiO5/BSAS/Si coating on Cf/SiC composites: processing and steam corrosion behavior

Recent progress on wet-oxygen corrosion resistance of SiC f /SiC composites

Oxidation Behavior of SiCf/SiC Composites Modified by Layered-Y2Si2O7 in Wet Oxygen Environment

Fabrication and oxidation resistance of mullite/yttrium silicate multilayer coatings on C/SiC composites

Long-term Ablation Behavior of Al4SiC4-YB4 SiC4-YB4 Modified Cf/ZrB2-SiC F /Zrb2-Sic Composites at 2600 °C