Abstract:Boron nitride-barium aluminosilicate (BN-BAS) composite ceramic specimens were prepared by using hot-press sintering at 1700 degrees C and 20 MPa from composite powders prepared by employing the sol-gel method. The dynamic compressive behaviors of these BN-BAS composite ceramic specimens were investigated by using split-Hopkinson-pressure-bar set-ups at room temperature and 1000 degrees C. The effects of the strain rate on the dynamic compressive strength, fragment size, and microstructure were investigated. The quasi-static mechanical properties of the composite ceramics were also tested. The results indicated that the quasi-static and dynamic mechanical properties of BN-BAS composite ceramics at 1000 degrees C were lower than those at room temperature, and this was caused by the crack propagation in the ceramic specimens at high temperatures owing to the high thermal expansion coefficient of hexacelsian. The dynamic compressive strength of the composite ceramic increased linearly with an increasing strain rate. Flake-like h-BN particles absorbed a large amount of energy through bridging and pull-out, which prevented macroscopic breakage of specimens at strain rates lower than 850 s(-1) at the initial failure stage at room temperature. As the strain rate increased, the cracks changed from long and sparse to small and dense reticularly distributed ones, and the fragment size decreased accordingly.

Fabrication and dynamic compressive response of reaction sintering H-BN ceramic

Compressibility And Strength Of Nanocrystalline Tungsten Boride Under Compression To 60gpa

Quasi-static and Dynamic Compressive Behavior of BN-BAS Composite Ceramic at Room Temperature and 1000 °C

Physical and mechanical properties of hexagonal boron nitride ceramic fabricated by pressureless sintering without additive

Analysis of Mechanical Properties of Al2O3‐cBN‐hBN Composites and Identification of Main Influencing Factors

Effect of Hexagonal BN on the Microstructure and Mechanical Properties of Pressureless Sintered Porous Si3N4 Ceramics

Fracture Behavior and Toughness of H-Bn/si_3n_4 Ceramic Composites

Fabrication of High Strength α-SiAlON/BN Composition Ceramics by Hot Pressing

Mechanical and wear properties of h-BN/Si3N4 ceramic composites

Fabrication and properties of Si3N4/BN composite ceramics by pressureless sintering with Yb2O3-Al 2O3-Y2O3 as sintering additives

The Study on the Property and the Microstructure of Pressureless Sintered h-BN Ceramics

Silicon nitride/boron nitride ceramic composites fabricated by reactive pressureless sintering

Effects of Weak Boundary Phases (WBP) on the Microstructure and Mechanical Properties of Pressureless Sintered Al2O3/h-BN Machinable Composites

Densification and mechanical properties of boron carbide prepared via spark plasma sintering with cubic boron nitride as an additive

Mechanical and tribological properties of hot-pressed h-BN/Si3N4 ceramic composites

Investigation of Fabrication and Properties of Machinable Si3N4/BN Nanocomposite Ceramics

Effects of H-Bn on Mechanical Properties of Reaction Bonded Β-Sialon/h-bn Composites

Fabrication and Properties of Pressureless Sintered Si3N4/BN Composite Ceramics with La2O3-Al2O3-Y2O3 as Sintering Additives

Fabrication of hexagonal boron nitride based ceramics by combustion synthesis

Influence of sintering pressure on the crystallization and mechanical properties of BN-MAS composite ceramics