Abstract:In this paper, we have examined the dopant activation levels in various materials (Si, SiGe, and Ge) annealed using two different microwave annealing (MWA) frequencies, 2.45 GHz and 5.8 GHz, with rapid thermal annealing serving as a comparative counterpart. The aim is to identify a material-specific annealing method that minimizes the high thermal budget typically required in the annealing process. For the dopant activation of Si wafer with B doping, there are two different frequencies (2.45 GHz and 5.8 GHz) MWA methods were compared. As the results of electrical measurement, the high activation level by 5.8 GHz MWA shows the material-targeted annealing method to reduce the thermal budget of the device. Additionally, we fabricated a high-k/metal gate (HKMG) MOSCAP structure, which was annealed using 2.45 GHz and 5.8 GHz MWA as part of the post-metallization annealing process. The results show that MWA at 2.45 GHz is more efficient than HF 5.8 GHz MWA at 3000 W in minimizing the interface trapped charge and the reduction in leakage current density. The highest capacitance (1.73 μF cm−2) was observed for MWA 2700 W at 2.45 GHz. However, there is a slight clear reduction in capacitance as the frequency increased to 5.8 GHz increasing in interfacial layer thickness. The post-metallization annealing of gate-last MOSCAPs using MWA at 2.45 GHz not only inhibits the growth of the equivalent oxide thickness and Al diffusion but also preserves the effects of pre-thermal annealing on doping activation at 5.8 GHz. Due to undesirable effects such as Al diffusion into the dielectric layer, the MWA at 5.8 GHz and 2.45 GHz demonstrates great a potential candidate, respectively as doping activation and as a post-metallization annealing method for HKMG structures.

Metal Boundary Effect Mitigation by HKMG Thermal Process Optimization in FinFET Integration Technology

NBTI Mitigation by Optimized HKMG Thermal Processing in a FinFET Technology

Improvement of Thermal and Mechanical Reliability of a LDMOS FET Using Graphene

Microstructure, optical and electrical properties of solution-derived peroxo-zirconium oxide gate dielectrics for CMOS application

Interface Optimization and Band Alignments of HfTiO/InGaAs Gate Stacks by Metalorganic Chemical Vapor Deposition of AlON Passivation Layer

Decoupled Plasma Nitridation (DPN) and Postnitridation Annealing (PNA) Treatment for Metal Boundary Effect Reduction

Early Effect for 28nm HK/MG PMOSFETs after Post Deposition Annealing Treatment

Alleviation of Negative-Bias Temperature Instability in Si P-Finfets with ALD W Gate-Filling Metal by Annealing Process Optimization

Impact of Post High-κ Deposition Anneal (PDA) and Post High-κ Capping Anneal (PCA) on the Xbti Performance in HfO2-Based FinFETs

Early effect exposing performance of 28nm HK/MG pMOSFETs under PDA or DPN nitridation treatment

Improving Low-Frequency Noise in 14-Nm FinFET by Optimized High-k/Metal Gate Thermal Processing

Thermal annealing, interface reaction, and lanthanum-based sub-nanometer EOT gate dielectrics

Fluorine IMP effect on negative bias temperature instability and process induced defects

Simulation Study of Metal-gate Work-function Optimization and the Impact on Device Performance in 32 nm Gate-last Process

Impact of Iterative Deuterium Annealing in Long-Channel MOSFET Performance

Study on NBTI improvement of HfO<inf>2</inf>-based 14 nm P-type FinFET with post high-k deposition thermal treatment

CLM effect for 28nm stacked HK nmosfets after DPN treatment with different annealing temperatures

Study on dopant activation and EOT impact in HKMG stacks using microwave annealing with different frequencies

Improvement of Aluminum Diffusion in HKMG Process

Effect of Rapid Thermal Annealing on DC Performance of Mg0.30Zn0.70O/Cd0.15Zn0.85O MOSHFET

Improved Gate Stability of Metal–Insulator–Semiconductor-High-Electron-Mobility Transistors with 10 Nm Atomic Layer Deposition Al2O3 by Tetramethylammonium Hydroxide Wet Treatment