Abstract:During the daily inspection process at a natural gas receiving station, ice was found to be present at the elbow of the pipeline, with a fog emerging from the elbow itself. This elbow was suspected of leaking. After investigation, it was found that the outer arc side of the elbow contained perforations resulting in the leaking of combustible gas. In this work, the causes for failure of such a low-temperature 304L stainless steel pipe elbow are analyzed and discussed. Macromorphological analysis, nondestructive testing analysis, chemical composition analysis, Charpy impact test, hardness test and microstructural analysis were performed to determine the root cause of the failure. The field investigation shows that the perforated failure pipe section is located downstream of the flow-limiting orifice plate, and that the pipe medium can contain small particles. Macroscopic observation reveals that the perforation defect is located at 3 points on the outer arc side, and the defect takes the shape of a bowl, with a perforation aperture diameter of approximately 0.7 mm. Microscopic observation reveals that the defective area has a honeycomb shape with tiny spheres on the surface, with many slip lines observed in the metallographic structure near the defect, indicating that the small deformation was caused by a large impact load. Based on the evidence of failure, the formation of the perforation defect is attributed to the excessive flow rate generated by the high pressure difference between the front and back sides of the single-stage orifice plate, which leads to the intensification of erosion. Moreover, when combined with the actual situation, it is found that the fine solid particles mixed in the medium can aggravate the thinning of the pipe wall section.

Analysis of Corrosion Failure Causes of Hongjing Line Crude Oil Pipeline

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Failure Analysis of A Pipeline in Sour Gas Field

Failure Causes Analysis of Circumferential Cracking on Gathering Pipeline in M Oil and Gas Field

Analysis of the corrosion failure causes of shale gas surface pipelines

Failure analysis of local effusion corrosion in small diameter gas pipeline: Experiment and numerical

Corrosion Failure Analyses of 20 Steel Pipeline for Hydrogen Transportation in Swampland

Insights into the perforation of the L360M pipeline in the liquefied natural gas transmission process

Internal localized corrosion of X65-grade crude oil pipeline caused by the synergy of deposits and microorganisms

Experimental and Numerical Analysis of the Impact of Corrosion on the Failure Pressure of API 5L X65 Pipeline

Analysis and investigation of the leakage failure on the shale gas gathering and transmission pipeline

Localised corrosion failure of an L245N pipeline in a CO2–O2–Cl− environment

Mechanical model and probability analysis of buried pipelines failure under uniform corrosion

Investigation of corrosion sequence in the overhead pipeline of H2S stripper column through CFD models

Failure analysis of leaking firefighting pipeline used in nuclear power plant: Corrosion development process and key influence factors

Corrosion Failure Analysis of a S135 Drill Pipe

Study on metal corrosion behavior of heat-affected zone of oil pipeline

Comprehensive analysis of corrosion failure of blast furnace gas pipeline in a steel plant

Failure Analysis on Abnormal Perforation of Super Large Diameter Buried Gas Pipeline Nearby Metro

Failure assessment of X80 pipeline with interacting corrosion defects

Perforation failure analysis of pipeline elbow at a receiving station