Abstract:During the daily inspection process at a natural gas receiving station, ice was found to be present at the elbow of the pipeline, with a fog emerging from the elbow itself. This elbow was suspected of leaking. After investigation, it was found that the outer arc side of the elbow contained perforations resulting in the leaking of combustible gas. In this work, the causes for failure of such a low-temperature 304L stainless steel pipe elbow are analyzed and discussed. Macromorphological analysis, nondestructive testing analysis, chemical composition analysis, Charpy impact test, hardness test and microstructural analysis were performed to determine the root cause of the failure. The field investigation shows that the perforated failure pipe section is located downstream of the flow-limiting orifice plate, and that the pipe medium can contain small particles. Macroscopic observation reveals that the perforation defect is located at 3 points on the outer arc side, and the defect takes the shape of a bowl, with a perforation aperture diameter of approximately 0.7 mm. Microscopic observation reveals that the defective area has a honeycomb shape with tiny spheres on the surface, with many slip lines observed in the metallographic structure near the defect, indicating that the small deformation was caused by a large impact load. Based on the evidence of failure, the formation of the perforation defect is attributed to the excessive flow rate generated by the high pressure difference between the front and back sides of the single-stage orifice plate, which leads to the intensification of erosion. Moreover, when combined with the actual situation, it is found that the fine solid particles mixed in the medium can aggravate the thinning of the pipe wall section.

Failure Analysis of A Pipeline in Sour Gas Field

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Failure analysis of local effusion corrosion in small diameter gas pipeline: Experiment and numerical

Failure Causes Analysis of Circumferential Cracking on Gathering Pipeline in M Oil and Gas Field

Analysis and investigation of the leakage failure on the shale gas gathering and transmission pipeline

Analysis of the corrosion failure causes of shale gas surface pipelines

Corrosion Failure Analyses of 20 Steel Pipeline for Hydrogen Transportation in Swampland

Mechanical model and probability analysis of buried pipelines failure under uniform corrosion

Probe into Water Chemistry Effects on Internal Corrosion Risk for Sour Gas Pipelines

Perforation failure analysis of pipeline elbow at a receiving station

Impact of Prolonged Exposure to Sour Service on the Mechanical Properties and Corrosion Mechanism of NACE Carbon Steel Material Used in Wet Sour Gas Multiphase Pipeline

Failure Analysis on Leakage and Perforation of Natural Gas Pipeline

On Collapse Failure Analysis Of Subsea Corroded Sandwich Pipelines Under External Pressure

Failure analysis of leaking firefighting pipeline used in nuclear power plant: Corrosion development process and key influence factors

Analysis Cracking Corrosion on Carbon Steel Pipes API 5L-X65 In Solution 7700 ml Aquades, 250 ml Acetic Acid and 50 ml Ammonia with Gas CO2 and H2S in Saturation Condition

Cause Analysis and Countermeasure for Submarine Pipeline Failure

Failure analysis of the collection pipeline at the outlet of air cooler in the distillation column

Reliability analysis of gas pipeline with corrosion defect based on finite element method

Sensitivity Analysis of Influencing Factors of Gas Pipelines with Corrosion Defects under the Action of Landslides

Corrosion failure analysis of the 45-degree elbow in a natural gas gathering pipeline by experimental and numerical simulation

Failure Analysis of Girth Weld Cracking in Gas Transmission Pipelines Subjected to Ground Subsidence and Traffic Loads