Abstract:Sandwich pipe (SP), consisting of two comparatively thin-walled metal tubes and a thick polymer or cement based core, is believed to be a feasible conception to transport hydrocarbons in deep sea. In this paper, the buckle propagation experiments were carried out on small-scale SP test specimens composed of two aluminium tubes and the polypropylene (PP) core. In association with experimental efforts, dedicated finite element models of SP test specimens under external pressure were established to reproduce the local collapse and consequent buckle propagating scenarios using the software ABAQUS, and good agreements were observed between the experimental and numerical results. Then, influencing mechanisms of inter-layer adhesion behaviour on the stress state, cross-section deformation and buckle propagation pressure of SPs were systematically studied, and broad parameter correlation analyses were performed to explore geometric and material properties of two steel tubes and polymer core on the buckle propagation pressure of SPs. The results show that good interface bonding conditions can markedly enhance the buckle propagation pressure of SPs and improve the energy dissipation and the deformation capacity of the structures. The core layer thickness and the ratio of the wall thickness between inner and outer tubes have extremely noticeable effect on the buckle propagation pressure of SPs. Additionally, based upon extensive numerical results, an empirical design expression was developed to conservatively estimate the buckle propagation pressure of SP systems for the no inter-layer adhesion case.

On Collapse Failure Analysis Of Subsea Corroded Sandwich Pipelines Under External Pressure

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

On Elastic-Plastic Collapse of Subsea Pipelines under External Hydrostatic Pressure and Denting Force

Buckle Propagation of Sandwich Pipes under External Pressure

Theoretical analysis of the collapse behaviour of subsea pipelines with corrosion defects under external pressure

On the Collapse Failure of Dented Pipes under Bending Moment and External Pressure

Local buckling of deepwater oil-gas pipeline under high hydrostatic pressure

Collapse of Dented Subsea Pipelines under External Pressure

Collapse failure and capacity of subsea pipelines with complex corrosion defects

Analysis on Buckling Performance of Submarine Pipelines During Deepwater Pipe-Laying Operation

On the Collapse of Thick-Walled Pipes with Corrosion Defects under External Pressure

Buckling Response of Offshore Pipelines under Combined Tension, Bending, and External Pressure

Buckling response of subsea pipeline with irregular corrosion defect under external pressure

Effect of Steel Properties on Buckling Pressure of Corroded Pipelines

Experimental and numerical studies on collapse of subsea pipelines with interacting corrosion defects

Asymmetric Collapse of Offshore Pipelines under External Pressure

Surface Stress Analysis of Internally Corroded Pipes under External Pressure

Buckling Response of Offshore Pipelines under Combined Tension and Bending

Buckle Propagation Analysis of Deep-Water Petroleum Transmission Pipelines with Axial Tension

Buckle Propagation of Offshore Pipelines under External Pressure

Buckling collapse of submarine thick-wall pipe under torque and hydraulic pressure based on vector form intrinsic finite element method