Theoretical analysis of the collapse behaviour of subsea pipelines with corrosion defects under external pressure
Libei Zhou,Shunfeng Gong,Lin Yuan,Xipeng Wang,Jin Huang
DOI: https://doi.org/10.1016/j.oceaneng.2024.118069
IF: 5
2024-05-19
Ocean Engineering
Abstract:Corrosion is considered as one of the most common defects, leading to a decrease in bearing capacity of pipelines in deep-water applications. In this study, the collapse performance of steel pipes with rectangular defects was studied through a combination of theoretical and numerical efforts. Based on the ring theory and virtual work principle, an extended theoretical model was established to predict the collapse pressure and failure mode of corroded pipes with symmetrical rectangular defects. Then, a numerical framework was developed to validate the reliability of the theoretical model. After that, extensive parametric analyses were carried out to explore the influence of major factors on the collapse pressure and failure mode, including key geometric parameters, material properties, as well as defect sizes and location. Five types of collapse pressure trajectories were observed under different defect locations due to the interactions between the defect and the initial imperfection. Also, the corroded pipes were found to exhibit the classical ovalization, U-shape, pear-shape, and anti-ovalization failure modes under different combinations of defect sizes and locations.
engineering, civil, ocean, marine,oceanography