Abstract:This paper employs the Finite Element Method (FEM) to simulate and analyze the effects of corrosion defect parameters on the stress and failure pressure of pipelines. It investigates how the boundary conditions of the pipeline model influence stress and examines the sensitivity of failure pressure to corrosion defect parameters. A nonlinear regression equation has been developed from a dataset obtained through simulation experiments to predict the failure pressure of corroded pipelines. To validate the effects of corrosion defect parameters on failure pressure, a hydrostatic test platform for an API 5L X65 pipeline with corrosion defects was established to measure stress levels and failure pressures across varying corrosion defects. This study reveals that failure pressure is negatively correlated with corrosion length and depth, while positively correlated with corrosion width. Among these parameters, corrosion depth exerts a more significant influence on the pipeline's failure pressure than corrosion length and width. Within the range of corrosion defect parameters examined, the maximum deviation of the prediction equation's results from the simulation results is 8.71%, with an average deviation of 5.81%. The standard deviation of the fitted residuals is 0.01837. Additionally, the maximum deviation between the predicted results and experimental measurements is 8.39%, with an average deviation of 7.77%. The strong agreement between the predicted results from the equation and the actual measured data underscores the effectiveness of the nonlinear regression equation.

Effect of the Y/T on the Burst Pressure for Corroded Pipelines with High Strength

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Double Circular Arc Model Based on Average Shear Stress Yield Criterion and Its Application in the Corroded Pipe Burst

Strength Differential Effect and Influence of Strength Criterion on Burst Pressure of Thin-Walled Pipelines

Estimation of burst pressure of pipeline using twin-shear stress yield criterion

On the effect of long corrosion defect and axial tension on the burst pressure of subsea pipelines

Integrity Assessment of the Pipelines Containing an Isolated Corrosion Pit

Burst Pressure of Pipelines with Plastic Anisotropy under Combined Internal and External Pressures

Surface Stress Analysis of Internally Corroded Pipes under External Pressure

The Failure Window Method and Its Application in Pipeline Burst

A Numerical Study on the High-Velocity Impact Behavior of Pressure Pipes

Failure pressure analysis of corroded moderate-to-high strength pipelines

Effect of Steel Properties on Buckling Pressure of Corroded Pipelines

Mechanical model and probability analysis of buried pipelines failure under uniform corrosion

Theoretical Assessment of Burst Failure of Internally Pressurized Defect-Free Pipelines with Plastic Anisotropy

Study on burst pressure of subsea pipelines with asymmetrical corrosion defects

Experimental and Numerical Analysis of the Impact of Corrosion on the Failure Pressure of API 5L X65 Pipeline

Analytical prediction of failure pressure for pipeline with long corrosion defect

Collapse of Corroded Pipelines under Combined Tension and External Pressure

Evaluating Fitness-for-Service of Corroded Metal Pipelines: Structural Reliability Bases

Burst Pressure Prediction of Subsea Supercritical CO2 Pipelines