Abstract:Background: With the continuous application of API 5L X100 high-strength grade steel pipeline and the development trend of increasing pipeline diameter and design pressure in China's long natural gas and petroleum pipeline, API 5L X100 high-strength grade steel pipeline steel is bound to become the aorta in long-distance pipeline construction in the future. Studying the failure pressure of API 5L X100 high-strength grade steel pipeline has high economic and social benefits Objective: Exploring the corrosion mechanism of the two single corroded pipeline models with outer defect and inner defect. objective: Using ANSYS Workbench 15.0 software to explore the two single corroded piping models with outer defect and inner defect. Methods: Using ANSYS Workbench 15.0 software to explore the two single corroded pipeline models with outer defect and inner defect and the influence of geometric parameters such as defect depth, defect length, defect width, etc., on the maximum equivalent stress and failure pressure investigated. Based on the finite element analysis database, the failure pressures of two single corroded pipeline models were fitted using Matlab software and the fitting formulas. Results: In the corrosion defect area of the pipeline, stress concentration occurs; Far away from the corrosion defect area, the stress distribution is uniform. For the pipeline model with outer defect and inner defect, as the defect depth and length increases, failure pressure shows a decreasing trend and is almost unaffected by defect width; As the ratio of diameter to thickness increases, failure pressure shows a decreasing trend; By fitting failure pressure formula of the pipeline models with outer defect and inner defect, a multivariate fitting function formula of failure pressure is obtained, with high fitting exactitude. Conclusion: The conclusion obtained have certain guiding values for the normal and stable operation of natural gas and petroleum transportation pipelines.

Experimental and Numerical Analysis of the Impact of Corrosion on the Failure Pressure of API 5L X65 Pipeline

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Research on Failure Pressure of API 5L X100 Pipeline with Single Defect

Failure Analysis of High Strength Pipeline with Single and Multiple Corrosions

Effect of the Y/T on the Burst Pressure for Corroded Pipelines with High Strength

Reliability and Residual Strength Analysis of Corroded Pipeline

Failure pressure analysis of corroded moderate-to-high strength pipelines

Finite element analysis of the failure of high-strength steel pipelines containing group corrosion defects

Effects of depth in external and internal corrosion defects on failure pressure predictions of oil and gas pipelines using finite element models

Failure assessment of X80 pipeline with interacting corrosion defects

Effect of Steel Properties on Buckling Pressure of Corroded Pipelines

Analytical prediction of failure pressure for pipeline with long corrosion defect

Evaluating Fitness-for-Service of Corroded Metal Pipelines: Structural Reliability Bases

Mechanical model and probability analysis of buried pipelines failure under uniform corrosion

Finite element modeling of corrosion defect growth and failure pressure prediction of pipelines

Bending Capacity of Corroded Pipeline Subjected to Internal Pressure and Axial Loadings

Surface Stress Analysis of Internally Corroded Pipes under External Pressure

Failure Pressure Evaluation of Corroded Pipeline Using Semi-Empirical and Finite Element Analysis

Finite element analyses of corroded pipeline with single defect subjected to internal pressure and axial compressive stress

Integrity Assessment of the Pipelines Containing an Isolated Corrosion Pit

Failure Pressure Analysis of the Pipe with Inner Corrosion Defects by FEM