Abstract:Suspension effect poses a big threat to the integrity and safety of corroded pipelines. In this work, a finite element (FE) based multi-physics field coupling model was developed to determine the mechano-electrochemical (M-E) interaction at an external corrosion defect on a suspended X100 steel pipe and predict its failure pressure. Theoretical calculations were used for model validation. Parameter effects including the defect location on the pipe, geometry of the defect, suspension length and pipe burial depth were determined. Results demonstared that, generally, the M-E effect at corrosion defect caused an increased stress concentration and anodic current density (i.e., corrosion rate), decreasing the failure pressure of the pipeline. The effect became more apparent when the pipe was in suspension. Both the stress and the anodic current density at the corrosion defect were dependent on the defect geometry, especially the defect depth. When the depth was up to 40% of pipe wall thickness, the von Mises stress exceeded the yield stress of the steel, causing local plastic deformation. A critical defect length of <math>20Dt</math> (D is the outer diameter of the pipe and t is pipe wall thickness) existed, below which the von Mises stress and the anodic current density at the corrosion defect increased with increased defect length. When the defect length exceeded the critical value, the effect was not obvious. An increased suspension length of the pipe would elevate the local stress and anodic current density at the corrosion defect, reducing the failure pressure of the pipe. A critical pipe burial depth of 2.5 m was identified, exceeding which the failure pressure of the pipe decreased rapidly with the increased burial depth. When the burial depth was smaller than 2.5 m, the effect was marginal. The location of the corrosion defect on the pipe did not affect the local stress, anodic current density and failure pressure at an appreciable level, and could be ignored in defect assessment on suspended pipelines.

Failure assessment of X80 pipeline with interacting corrosion defects

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Assessment by finite element modeling of the interaction of multiple corrosion defects and the effect on failure pressure of corroded pipelines

Finite element analysis of the failure of high-strength steel pipelines containing group corrosion defects

Experimental and Numerical Analysis of the Impact of Corrosion on the Failure Pressure of API 5L X65 Pipeline

Effect of interaction between corrosion defects on failure pressure of thin wall steel pipeline

Research on Failure Pressure of API 5L X100 Pipeline with Single Defect

Study on Evaluation Method of Failure Pressure for Pipeline with Axially Adjacent Defects

Assessment of the interaction of corrosion defects on steel pipelines under combined internal pressure and longitudinal compression using finite element analysis

Analytical prediction of failure pressure for pipeline with long corrosion defect

Failure pressure prediction by defect assessment and finite element modelling on natural gas pipelines under cyclic loading

Finite element modeling of corrosion defect growth and failure pressure prediction of pipelines

Failure pressure analysis of corroded moderate-to-high strength pipelines

Assessment on failure pressure of high strength pipeline with corrosion defects

Effects of depth in external and internal corrosion defects on failure pressure predictions of oil and gas pipelines using finite element models

Failure Pressure Analysis of the Pipe with Inner Corrosion Defects by FEM

Buckling response of subsea pipeline with irregular corrosion defect under external pressure

A novel strain-based assessment method of compressive buckling of X80 corroded pipelines subjected to bending moment load

Experimental and numerical studies on collapse of subsea pipelines with interacting corrosion defects

Study on Assessment Method of Failure Pressure for Pipelines with Colony Corrosion Defects Based on Failure Location

Modeling of mechano-electrochemical interaction at a corrosion defect on a suspended gas pipeline and the failure pressure prediction