Abstract:Abstract Aging pipelines may experience several different types of degradation, such as crack and corrosion, which pose serious concerns for the pipeline integrity. Hybrid flaws such as crack-in-corrosion (CIC), can be challenging to model and understand. For instance, predicting the failure pressure using the finite element method (FEM) is relatively difficult; therefore, the extended finite element method (XFEM) is introduced here. Compared to the conventional FEM, which requires extremely fine meshes and is impractical for modelling dynamic crack propagation, XFEM is computationally efficient as there is no need to update the mesh elements for tracking the crack path. This paper aims to study the applicability of XFEM in predicting the failure pressure of CIC defects in 2D. In particular, mesh size sensitivity and the effects of different CIC parameters on the final failure pressure were examined. ABAQUS v 6.14 was used for this simulation study. For simplicity, only half of the pipe was modelled assuming symmetry around the horizontal plane. A CIC defect was placed at the exterior of the pipe. The corroded area was assumed to be semi-elliptical, and the crack was simulated as a longitudinal crack. In this paper, failure criterion was satisfied when the crack has propagated to the last element. Several models were built in which the length and width of the elements at the crack tip were changed. An optimum mesh size was determined and was applied subsequently in several other models to study the impacts of crack depths, corroded area widths, and corrosion profiles. The results showed that when the total defect depth was fixed at 50% of the wall thickness, the failure pressure decreased with increasing the crack depth, while both corroded area width and corrosion profile only have a secondary effect on the failure pressure. In addition, the failure pressure of a CIC defect was bound between that of a crack-only defect and a corrosion-only defect. When the depth of the crack is higher than 50% of the total defect area, the CIC defect can be treated as a crack only defect with a crack depth equal to the total defect depth.

Failure pressure prediction by defect assessment and finite element modelling on natural gas pipelines under cyclic loading

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Finite element modeling of corrosion defect growth and failure pressure prediction of pipelines

Modeling of mechano-electrochemical interaction at a corrosion defect on a suspended gas pipeline and the failure pressure prediction

Analytical prediction of failure pressure for pipeline with long corrosion defect

Research on Failure Pressure of API 5L X100 Pipeline with Single Defect

Finite element analysis of the failure of high-strength steel pipelines containing group corrosion defects

Failure pressure prediction by defect assessment and finite element modelling on pipelines containing a dent-corrosion defect

Failure pressure analysis of corroded moderate-to-high strength pipelines

Assessment by finite element modeling of the interaction of multiple corrosion defects and the effect on failure pressure of corroded pipelines

Failure assessment of X80 pipeline with interacting corrosion defects

Effects of depth in external and internal corrosion defects on failure pressure predictions of oil and gas pipelines using finite element models

Assessment on failure pressure of high strength pipeline with corrosion defects

Development of an empirical model to predict the burst pressure of corroded elbows of pipelines by finite element modelling

Failure Pressure Prediction of Crack in Corrosion Defects in 2D by Using XFEM

Failure Pressure Analysis of the Pipe with Inner Corrosion Defects by FEM

Research On Safety Assessment Method For Pressure Pipe With Incomplete Welding Defects Under Complicated Loadings

Predicting the Failure Pressure of Pipelines Containing Nonuniform Depth Corrosion Defects Using the Finite Element Method

Safety and reliability assessment of external corrosion defects assessment of buried pipelines—soil interface: A mechanisms and FE study

Failure analysis of natural gas buried X65 steel pipeline under deflection load using finite element method

Pipeline condition assessment and finite element modeling of mechano-electrochemical interaction between corrosion defects with varied orientations on pipelines