Abstract:Initial geometric imperfections and corrosion defects were considered as two of the most common imperfections for subsea pipes, which could lead to an inevitable reduction of collapse capacity. In this study, the coupling effect of both types of defects on the collapse performance was investigated numerically, with a particular focus on the relative corrosion position as described by defect location angle (DLA). A customised numerical framework was established to efficiently build FE models with various corrosion defects and imperfect geometry. Verification of the finite element (FE) model was performed using existing experiments in the open literature. In addition, extensive sensitivity studies were then conducted for several key problem parameters, including defect length, width, depth, initial ovality, and DLA. The variation of normalised collapse pressure with DLA exhibits two types of trajectories, namely 'Minor Decrease' and 'Constant-Decrease-Constant' responses. In the first, the normalised collapse pressure decreases slightly with increasing DLA. Among these cases, if the ratio stays above or close to 1.0, the collapse takes the form of classical ovalization mode. In contrast, for cases below 1.0, the collapse occurs in the corroded region. For the latter type of trajectory, the normalised collapse pressure follows a 'Constant-Decrease-Constant' path, and the collapse mode involves ovalization, anti-ovalization, non-symmetrical and U-shaped pattern. Subsequently, a series of empirical formulas were proposed upon extensive simulation results to predict the collapse pressure of non-symmetrical defect pipes.

Collapse failure and capacity of subsea pipelines with complex corrosion defects

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

On Collapse Failure Analysis Of Subsea Corroded Sandwich Pipelines Under External Pressure

Experimental and numerical studies on collapse of subsea pipelines with interacting corrosion defects

Theoretical analysis of the collapse behaviour of subsea pipelines with corrosion defects under external pressure

On Elastic-Plastic Collapse of Subsea Pipelines under External Hydrostatic Pressure and Denting Force

Collapse of Dented Subsea Pipelines under External Pressure

On the Collapse of Thick-Walled Pipes with Corrosion Defects under External Pressure

Collapse of Corroded Pipelines under Combined Tension and External Pressure

Mechanical model and probability analysis of buried pipelines failure under uniform corrosion

Study on burst pressure of subsea pipelines with asymmetrical corrosion defects

Effect of the Y/T on the Burst Pressure for Corroded Pipelines with High Strength

Effect of Steel Properties on Buckling Pressure of Corroded Pipelines

Buckling response of subsea pipeline with irregular corrosion defect under external pressure

Effect of chord-cut defects on the collapse response of thick-walled pipelines

Integrity Assessment of the Pipelines Containing an Isolated Corrosion Pit

Experimental and Numerical Analysis of the Impact of Corrosion on the Failure Pressure of API 5L X65 Pipeline

On the collapse of thick-walled steel pipes under coupling initial geometric imperfection and corrosion defect

Surface Stress Analysis of Internally Corroded Pipes under External Pressure

On the effect of long corrosion defect and axial tension on the burst pressure of subsea pipelines

On the Collapse Failure of Dented Pipes under Bending Moment and External Pressure