Abstract:The current study highlights the corrosion consequences observed in API 5L X65 carbon steel when exposed to a marine-like environment containing carbon dioxide (CO2), in the presence of sulfate- reducing bacteria consortium (C-SRB), iron-reducing bacteria consortium (C-IRB), and a combination of both (C-SRB+C-IRB). The corrosion behaviour was assessed through the utilisation of weight loss and surface analysis techniques. The biofilms and corrosion products were characterised using field emission scanning electron microscopy (FESEM) and infinite focus microscope (IFM), respectively. The results obtained from the weight loss technique provided confirmation that in the absence of bacteria, uniform corrosion was the prevailing mechanism in the medium. The uniform corrosion rate was found to be 0.95 mm/year, which was higher than the pit penetration rate of 0.28 mm/year. The combined actions of the C-SRB+C-IRB consortium result in a synergistic impact, leading to a significantly higher rate of pit penetration compared to the individual activities of SRB. Specifically, the pit penetration rate value of 2.13 mm/year is observed, which is notably higher than the uniform corrosion rate of 0.59 mm/year. The utilisation of surface analysis techniques has shown evidence of the existence of sulfur on carbon steel samples that were subjected to exposure from the C-SRB+C-IRB consortium in a CO2 environment. This sulphur presence is believed to potentially play a role in the development of the iron sulphide (FeS) layer. FeS presence is a contributing factor to the occurrence of pit corrosion due to the SRB metabolite activities. The activities of these metabolites readily dissolve in the medium, hence altering the chemical interface properties of both the metal and the biofilm. For specimens exposed to C-SRB only, the results obtained were almost identical to exposure to the C- SRB+C-IRB consortium. However, the corrosion rate value measured for the C-SRB+C-IRB consortium was higher due to the synergistic effect of the two bacteria. In conclusion, the presence of C-SRB alone and the consortium of C-SRB+C-IRB in a CO2 environment induces the formation of pitting corrosion. The findings of this study are presumed to contribute a deep understanding of the microbiology-influenced corrosion (MIC) mechanism in CO2 environments troubling the oil and gas industry. With a better understanding of MIC, new and improved corrosion prevention strategies can be put into action.

Impact of Prolonged Exposure to Sour Service on the Mechanical Properties and Corrosion Mechanism of NACE Carbon Steel Material Used in Wet Sour Gas Multiphase Pipeline

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Probe into Water Chemistry Effects on Internal Corrosion Risk for Sour Gas Pipelines

A study on the microbial biocorrosion behavior of API 5 L X65 carbon steel exposed to seawater

Corrosion behavior study on heat treated API X70 pipeline steel exposed in different aggressive environments

Carbon Steel X65QS Pipeline Qualification for Extreme Sour Service a Global Approach: Line Pipe, Welding, Eca Methodology and Diyab Pipeline Case Study

Corrosion Investigation of Commercially Available Linepipe Steel in CO2 Environment

Experimental Investigation of the Effects of Different Environmental Conditions on Pipelines Corrosion Rates

Corrosion Behavior of AISI 316L Stainless Steel in a Highly Sour Environment

Failure Analysis of A Pipeline in Sour Gas Field

Effect of seawater salinity, pH, and temperature on external corrosion behavior and microhardness of offshore oil and gas pipeline: RSM modelling and optimization

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Microbial corrosion behavior of pipeline steels in simulation environment of natural gas transportation pipeline

An Investigation on the causes of corrosion in AISI 1009 steel pipe of the fire line in the gas refinery

Analysis Cracking Corrosion on Carbon Steel Pipes API 5L-X65 In Solution 7700 ml Aquades, 250 ml Acetic Acid and 50 ml Ammonia with Gas CO2 and H2S in Saturation Condition

Performance of two high-strength steels under electrochemical corrosive and stressed conditions

Influence of Sulfate and Iron Reducing Bacteria on Carbon Steel Corrosion in Marine Environments

Methanogenic Archaea and Sulfate Reducing Bacteria Induce Severe Corrosion of Steel Pipelines after Hydrostatic Testing

Corrosion of API 5L X60 Pipeline Steel in Soil and Surface Defects Detection by Ultrasonic Analysis

Examining the Impact of Producer Gas in Specific Regions of Pipeline Materials of Producer Gas Systems