Abstract:The current study highlights the corrosion consequences observed in API 5L X65 carbon steel when exposed to a marine-like environment containing carbon dioxide (CO2), in the presence of sulfate- reducing bacteria consortium (C-SRB), iron-reducing bacteria consortium (C-IRB), and a combination of both (C-SRB+C-IRB). The corrosion behaviour was assessed through the utilisation of weight loss and surface analysis techniques. The biofilms and corrosion products were characterised using field emission scanning electron microscopy (FESEM) and infinite focus microscope (IFM), respectively. The results obtained from the weight loss technique provided confirmation that in the absence of bacteria, uniform corrosion was the prevailing mechanism in the medium. The uniform corrosion rate was found to be 0.95 mm/year, which was higher than the pit penetration rate of 0.28 mm/year. The combined actions of the C-SRB+C-IRB consortium result in a synergistic impact, leading to a significantly higher rate of pit penetration compared to the individual activities of SRB. Specifically, the pit penetration rate value of 2.13 mm/year is observed, which is notably higher than the uniform corrosion rate of 0.59 mm/year. The utilisation of surface analysis techniques has shown evidence of the existence of sulfur on carbon steel samples that were subjected to exposure from the C-SRB+C-IRB consortium in a CO2 environment. This sulphur presence is believed to potentially play a role in the development of the iron sulphide (FeS) layer. FeS presence is a contributing factor to the occurrence of pit corrosion due to the SRB metabolite activities. The activities of these metabolites readily dissolve in the medium, hence altering the chemical interface properties of both the metal and the biofilm. For specimens exposed to C-SRB only, the results obtained were almost identical to exposure to the C- SRB+C-IRB consortium. However, the corrosion rate value measured for the C-SRB+C-IRB consortium was higher due to the synergistic effect of the two bacteria. In conclusion, the presence of C-SRB alone and the consortium of C-SRB+C-IRB in a CO2 environment induces the formation of pitting corrosion. The findings of this study are presumed to contribute a deep understanding of the microbiology-influenced corrosion (MIC) mechanism in CO2 environments troubling the oil and gas industry. With a better understanding of MIC, new and improved corrosion prevention strategies can be put into action.

Methanogenic Archaea and Sulfate Reducing Bacteria Induce Severe Corrosion of Steel Pipelines after Hydrostatic Testing

Microbial corrosion behavior of pipeline steels in simulation environment of natural gas transportation pipeline

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Severe Microbial Corrosion of L245 Transportation Pipeline Triggered by Wild Sulfate Reducing Bacteria in Shale Gas Produced Water

Corrosion of Q235 carbon steel induced by sulfate-reducing bacteria in groundwater: corrosion behavior, corrosion product, and microbial community structure

A study on the microbial biocorrosion behavior of API 5 L X65 carbon steel exposed to seawater

The Microbiologically Influenced Corrosion and Protection of Pipelines: A Detailed Review

Influence of initial pH and sulfate‐reducing bacteria concentration on the microbiologically influenced corrosion of buried pipeline steel

Experimental study on pipeline corrosion behavior coupled with microorganisms and dynamic alternating current interference

Insight into sulfate-reducing bacteria corrosion behavior of X80 pipeline steel welded joint in a soil solution

Corrosion of Sulfate-Reducing Bacteria on L245 Steel under Different Carbon Source Conditions

Microbial Corrosion of API 5L X-70 Carbon Steel by ATCC 7757 and Consortium of Sulfate-Reducing Bacteria

Influence of anion and sulfate-reducing bacteria on the stress corrosion behavior and mechanism of X70 steel in a marine mud environment

Accelerated corrosion of pipeline steel in the presence of Desulfovibrio desulfuricans biofilm due to carbon source deprivation in CO2 saturated medium

Investigating the effects of environment, corrosion degree, and distribution of corrosive microbial communities on service-life of refined oil pipelines

Influence of Sulfate and Iron Reducing Bacteria on Carbon Steel Corrosion in Marine Environments

Investigation of carbon steel corrosion by oilfield nitrate- and sulfate-reducing prokaryotes consortia in a hypersaline environment

Microbiologically influenced corrosion of steel in coastal surface seawater contaminated by crude oil

Responses of Microbial Community Composition to Temperature Gradient and Carbon Steel Corrosion in Production Water of Petroleum Reservoir

The synergistic effect of parallel magnetic field and sulfate-reducing bacteria on stress corrosion cracking of buried X80 pipeline steel

Corrosion under insulation of pipeline steel in groundwater containing sulphate-reducing bacteria