Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Localised corrosion failure of an L245N pipeline in a CO2–O2–Cl− environment

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Investigation into main controlling factors and prediction model of L245NS steel corrosion rate in CO2–O2–SO2–H2S–H2O environment

Study on Corrosion Characteristics of Heat-resistant Materials in Supercritical Carbon Dioxide Environment Containing Oxygen Impurities

Effect of Temperature on the Corrosion Behavior of L245NS Steel in a CO2/H2S/O2 Multi-component Thermal Fluid Collection and Transportation System

Effect Of Temperature On Corrosion Behaviour Of X70 Steel In High Pressure Co2/So2/O-2/H2o Environments

Impact of O2 Content on the Corrosion Behavior of X65 Mild Steel in Gaseous, Liquid and Supercritical CO2 Environments

CO2-O2-SRB-Cl− Multifactor Synergistic Corrosion in Shale Gas Pipelines at a Low Liquid Flow Rate

Effect of H2S concentrations on corrosion failure of L245NS steel in CO2-O2-H2S system

Experimental Study on Corrosion Performance of Oil Tubing Steel in HPHT Flowing Media Containing O2 and CO2

Failure analysis of local effusion corrosion in small diameter gas pipeline: Experiment and numerical

Study on Corrosion Mechanism of N80 Steel Pipe Columns and Threads by CO2-Cl− in Shale Gas

Effect of Flow on the Corrosion Behavior of Pipeline Steel in Supercritical CO2 Environments with Impurities

Effect of High-Concentration O2on Corrosion Behavior of X70 Steel in Water-Containing Supercritical CO2with SO2

Factors Influencing the CO2 Corrosion Pattern of Oil–Water Mixed Transmission Pipeline during High Water Content Period

Failure analysis of corrosion products formed during CO2 pre-corrosion of X70 and 3Cr steels: Effect of oxygen contamination

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Experimental Study on Corrosion of J55 Casing Steel and N80 Tubing Steel in High Pressure and High Temperature Solution Containing CO2 and NaCl

Study on the Corrosion Mechanism of N80 Steel in Simulated Oxygen-Reduced Air Drive Production Wellbores

Insights into the perforation of the L360M pipeline in the liquefied natural gas transmission process