Insights into the perforation of the L360M pipeline in the liquefied natural gas transmission process

Xuanpeng Li,Qingguo Chen,Chengzheng Li,Xiaobo Zhang,Gen Tong,Peng Cui,Linfeng Lu,Qingwei Ma,Juntao Yuan,Anqing Fu,Chengxian Yin,Yaorong Feng

DOI: https://doi.org/10.1016/j.engfailanal.2022.106566

IF: 4

2022-10-01

Engineering Failure Analysis

Abstract:The cause of the failure of a liquefied natural gas transmission pipeline that has experienced internal corrosion during the water injection, idle and transmission processes, is fully investigated in this work. There are two significant features of pipeline failure, namely, the perforated location at the 6o’clock position and under scales deposit. Hence, the 2# leakage point and corrosion scale character were investigated in this research. The perforation of pipeline is attributed to three consecutive stages: (a)corrosion scale formation and pitting initiated, (b) the thickening of the scales and pitting propagation, and (c) the deposit of scales and pitting growth. Among of that, the deposited scales accelerate the pits growth during the LNG transmission process. Meanwhile, the premise cause of the failure was the scales deposit and pits initiation, pits propagation caused in water injection and idle processes.

engineering, mechanical,materials science, characterization & testing