Abstract:We aimed to investigate the corrosion patterns and the main controlling factors of N80 steel and P110 steel tubing under different sections. Conducting weight loss corrosion experiments for 168 h using high-temperature and high-pressure autoclaves to simulate the corrosion behavior of two types of casing materials, N80 steel and P110 steel, in different well sections under specific conditions of CO2 content, chloride ion concentration, temperature, pressure, and sulfate-reducing bacteria population in highly mineralized formation water. X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDS) were used to analyze the corrosion products, surface morphology, and elemental composition of the two steel pipes. Additionally, 3D microscopy was employed to observe the morphology and measure the dimensions of localized corrosion pits. Under different well sections, the corrosion products formed on N80 steel and P110 steel mainly consist of FeCO3, and crystalline salts of chlorides present in the solution medium. Under low-water-cut conditions, narrow and deep corrosion defects were observed, while narrow and shallow corrosion defects were found under high-water-cut conditions. In the upper wellbore section, both steel pipes exhibited dispersed and thin corrosion product films that suffered from rupture and detachment, resulting in severe localized corrosion. In the middle wellbore section, the corrosion product film on N80 steel comprised irregularly arranged polygonal grains, some of which exhibited significant gaps, leading to extremely severe corrosion. For P110 steel, the corrosion product film was also dispersed and thin, with extensive detachment and extremely severe corrosion. In the lower wellbore section, both steel pipes were covered with a dense layer of grains, with smaller gaps between them, effectively protecting the metal matrix from corrosion. Consequently, the corrosion rate decreased compared to the middle section but still exhibited severe corrosion. In low-water-cut conditions, attention should be given to the risk of column safety due to corrosion from condensate water and CO2, as well as the size of narrow and deep corrosion defects in the middle wellbore section. In high-water-cut conditions, it is recommended to use corrosion inhibitors in combination while focusing on SRB bacteria corrosion in the upper wellbore section, condensate water in the middle section, CO2 content and chloride ion coupling in the lower section, and the size of narrow and shallow corrosion defects causing column safety risks.

CO2-O2-SRB-Cl− Multifactor Synergistic Corrosion in Shale Gas Pipelines at a Low Liquid Flow Rate

Factors Influencing the CO2 Corrosion Pattern of Oil–Water Mixed Transmission Pipeline during High Water Content Period

Analysis of the corrosion failure causes of shale gas surface pipelines

Corrosion main control factors and corrosion degree prediction charts in H2S and CO2 coexisting associated gas pipelines

Localised corrosion failure of an L245N pipeline in a CO2–O2–Cl− environment

Main control factors and prediction model of flow-accelerated CO2/H2S synergistic corrosion for X65 steel

Study on Corrosion Mechanism of N80 Steel Pipe Columns and Threads by CO2-Cl− in Shale Gas

Microbial corrosion behavior of pipeline steels in simulation environment of natural gas transportation pipeline

Flow Influenced Initiation and Propagation of SRB Corrosion on L360N Carbon Steel

Experimental and numerical simulation of erosion-corrosion of 90° steel elbow in shale gas pipeline

Probe into Water Chemistry Effects on Internal Corrosion Risk for Sour Gas Pipelines

Effect of Flow on the Corrosion Behavior of Pipeline Steel in Supercritical CO2 Environments with Impurities

Research Progress on Corrosion Behavior of Oil and Gas Pipelines in Wet CO2 and H2S Environments

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Corrosion Mechanism of Oil Field Gathering Pipeline Containing Small H2S Impurity

Simulation of the Modes of Medium Flow Movement through a Gas Pipeline during Corrosion Tests

Corrosion of Sulfate-Reducing Bacteria on L245 Steel under Different Carbon Source Conditions

Investigation into main controlling factors and prediction model of L245NS steel corrosion rate in CO2–O2–SO2–H2S–H2O environment

A novel liquid pipeline internal corrosion direct evaluation technology and the application on the water pipeline

Failure analysis of CO2 corrosion of natural gas pipeline under flowing conditions

Research on the Multifactor Synergistic Corrosion of N80 and P110 Steel Tubing in Shale Gas Wells in Sichuan Basin