Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Failure analysis of CO2 corrosion of natural gas pipeline under flowing conditions

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

The Effect of Flowing Velocity and Impact Angle on the Fluid-Accelerated Corrosion of X65 Pipeline Steel in a Wet Gas Environment Containing CO2

Effect of Flow on the Corrosion Behavior of Pipeline Steel in Supercritical CO2 Environments with Impurities

Study on Corrosion Mechanism of N80 Steel Pipe Columns and Threads by CO2-Cl− in Shale Gas

Analysis of Internal Corrosion of Supercritical CO2 Pipeline

Failure analysis of local effusion corrosion in small diameter gas pipeline: Experiment and numerical

Failure Analysis on Leakage and Perforation of Natural Gas Pipeline

CFD-Based Erosion and Corrosion Modeling of a Pipeline with CO2-Containing Gas–Water Two-Phase Flow

Corrosion behavior of X80 pipeline steel local defect pits under static liquid film

Study on corrosion properties of pipelines in simulated produced water saturated with supercritical CO2

Research progress and risk analysis on internal corrosion of carbon dioxide pipeline steel with the influence of impurities

Corrosion Behavior of Oil Tube Steels under Conditions of Multiphase Flow Saturated with Super-Critical Carbon Dioxide

Effect Of Temperature On Corrosion Behaviour Of X70 Steel In High Pressure Co2/So2/O-2/H2o Environments

Corrosion Investigation of Commercially Available Linepipe Steel in CO2 Environment

Effect of Exposure Time on the Corrosion Rates of X70 Steel in Supercritical CO2/SO2/O2/H2O Environments

Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions

Evaluation of corrosion and erosion–corrosion behavior of X65 pipeline steel in flowing CO2-saturated electrolyte

Corrosion of pipeline steel in dense phase CO2 containing impurities: A critical review of test methodologies

Internal localized corrosion of X100 pipeline steel under simulated flow conditions