Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

The Effect of Flowing Velocity and Impact Angle on the Fluid-Accelerated Corrosion of X65 Pipeline Steel in a Wet Gas Environment Containing CO2

Effect of Flow on the Corrosion Behavior of Pipeline Steel in Supercritical CO2 Environments with Impurities

Evaluation of corrosion and erosion–corrosion behavior of X65 pipeline steel in flowing CO2-saturated electrolyte

Failure analysis of CO2 corrosion of natural gas pipeline under flowing conditions

Flow-Assisted Corrosion of API 5L X56 Steel: Effect of Flow Velocity and Dissolved Oxygen

Effect Of Temperature On Corrosion Behaviour Of X70 Steel In High Pressure Co2/So2/O-2/H2o Environments

INFLUENCE OF TEMPERATURE,CO_2 PARTIAL PRESSURE, FLOW RATE AND pH VALUE ON UNIFORM CORROSION RATE OF X65 PIPELINE STEEL

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

CFD-Based Erosion and Corrosion Modeling of a Pipeline with CO2-Containing Gas–Water Two-Phase Flow

Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions

Main control factors and prediction model of flow-accelerated CO2/H2S synergistic corrosion for X65 steel

Effects of fluid dynamics Parameters on flow-accelerated corrosion at elbow of carbon steel pipeline

Corrosion Behavior of Oil Tube Steels under Conditions of Multiphase Flow Saturated with Super-Critical Carbon Dioxide

Effect of Jet Impingement Velocity and Angle on CO2 Erosion–Corrosion with and without Sand for API 5L-X65 Carbon Steel

Characterization of Flow-Accelerated-corrosion of Pressure Piping Welded Joints

Electrochemical Investigation of the Corrosion Behavior of API 5L-X65 Carbon Steel in Carbon Dioxide Medium

Microstructural Understanding of Flow Accelerated Corrosion of SA106B Carbon Steel in High-Temperature Water with Different Flow Velocities

Impact of Surface Roughness and Humidity on X70 Steel Corrosion in Supercritical CO2 Mixture with SO2, H2O, and O2

Effect of Rotating Speed and Hydrostatic Pressure on Erosion- Corrosion Behavior of X65 Pipeline Steel

Corrosion behaviour of X80 pipeline steel welded joint in H2O- saturated supercritical-CO2 environment

Corrosion Behavior of X65 Pipeline Steel: Comparison of Wet–dry Cycle and Full Immersion