Abstract:Since the period required for testing the atmospheric corrosion of steel is long, most studies have focused on the corrosion behavior in less than three years, making exploring long-term atmospheric corrosion particularly valuable. This study investigates the corrosion behaviors, corrosion models, and mechanical properties of Q235 welded steel pipes collapsing due to corrosion after 25-year service in an urban industrial atmospheric environment using SEM, XRD, electrochemical methods, 3-D noncontact surface profilometry, and static tensile testing. The typical morphologies of & alpha;-FeOOH, & gamma;-FeOOH, and Fe3O4 and the effect of the content of various corrosive materials on the corrosion rate of the steel pipes are identified and analyzed. Then, the influence of different corrosion degrees on the mechanical properties of the steel pipes is examined by considering the morphologies of the rust pits. The results show that the wetting-drying cycles affect the structures of the rust layers and their protective properties. The rust layers on the sheltered surface are thicker but less protective than those on the exposed surface. In the wet state, FeSO4 accelerates ion transfer, while Fe3O4 facilitates electron transfer. These processes collectively contribute to the corrosion of Q235 steel. Moreover, as the time-of-wetness of the rust layers on sheltered specimens increases, the corrosion rate of Q235 steel also accelerates. The corrosion model combines pitting and uniform corrosion and gradually changes from predominated by pitting to thickness as the corrosion degree increases. The corrosion morphology impacts the mechanical properties of the welded steel pipes, and the influences of the thickness loss and maximum rust pit depth on these properties are profound.

Characterization of Flow-Accelerated-corrosion of Pressure Piping Welded Joints

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

The Corrosion Resistance of 0cr19ni9 Stainless Steel Arc Welding Joints with and Without Arc Surface Melting

Flow-Accelerated Corrosion Damage in a Steam Pipe Girth Weld

Study on High-Temperature Naphthenic Acid Corrosion of Type 304 and Type 316L Stainless Steel and Their Welded Joints

Comparative investigation on high-pressure flow accelerated corrosion at gradual contraction and gradual expansion pipes

Microstructural Understanding of Flow Accelerated Corrosion of SA106B Carbon Steel in High-Temperature Water with Different Flow Velocities

Corrosion Behavior of 16mnr Steel and Welded Joints in High-Temperature Naphthenic Acid

The Effect of Flowing Velocity and Impact Angle on the Fluid-Accelerated Corrosion of X65 Pipeline Steel in a Wet Gas Environment Containing CO2

On-Line Measurement and Characterization of Electrochemical Corrosion of 304L Stainless Steel Pipe Wall in High-Speed Cl-Containing Solution

Erosion–Corrosion Behavior of Friction Stud Welded Joints of X65 Pipelines in Simulated Seawater under Different Flow Rates

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Flow-Assisted Corrosion of API 5L X56 Steel: Effect of Flow Velocity and Dissolved Oxygen

Decoupling the role of microstructure and geometric discontinuity introduced by weld reinforcement height on corrosion behavior of SA106B/316L SS welded joint in the flowing 0.5 M NaCl solution

Pitting Corrosion Resistance of Welded Joints of a Super-duplex Stainless Steel by Electrochemical Characteristics Analysis

Corrosion behaviour of 316L stainless steel and anti-corrosion materials in a high acidified chloride solution

Corrosion performance of super duplex stainless steel and pipeline steel dissimilar welded joints: a comprehensive investigation for marine structures

Technical Note: Study on Accelerated Corrosion Behavior and Mechanism of X80 Pipeline Steel Welded Joint under Cyclic Salt Spray Test

Study on metal corrosion behavior of heat-affected zone of oil pipeline

STUDY ON THE ACCELERATED CORROSION BEHAVIOR OF A GALVANIZED X80 PIPELINE STEEL WELDED JOINT DURING A CYCLIC SALT SPRAY TEST